The Bi-2223/Ag tapes were prepared with spray-died powders, which are of different particle sizes and phase assemblages by varying the annealing time in pure oxygen. Longer time annealing degraded the reactivity of precursor powder, which in turn resulted in an incomplete conversion from precursors to Bi-2223, porosity core and misaligned grains in fully processed tapes. The best Jc in short pressed samples varied from 29.7 to 47kA/cm2 for the tapes made from different powders.
The Bi-2223 / Ag tapes were prepared with spray-died powders, which are of different particle sizes and phase assemblages by varying the annealing time in pure oxygen. Longer time annealing degrade the reactivity of precursor powder, which in turn resulted in an incomplete conversion from precursors to Bi-2223, porosity core and misaligned grains in fully processed tapes. The best Jc in short pressed samples varied from 29.7 to 47 kA / cm2 for the tapes made from different powders.