水口水电站船闸工程抗磨蚀部位通过使用ＮＳＦ剂和粉煤灰共掺混凝土，在单方水泥用量仅２５５ｋｇ／ｍ３情况下配制出９０ｄ抗压强度达８６．３ＭＰａ（机口采样平均值）的混凝土，其抗冲磨能力比普通混凝土提高回倍，抗空蚀能力提高４倍。通过掺用的ＮＳＦ剂中的膨胀剂补偿硅粉混凝土的早期收缩及加强早期潮湿雾化养护、解决了硅粉混凝土早期收缩偏大的难题，在水口工程的成功应用证明ＮＳＦ剂是一种可以推广应用的新材料。
Anti-erosion site of shiplock project of Shuikou Hydropower Station Concrete was prepared with 90d compressive strength of 86.3MPa (the average of port sampling) by using NSF agent and fly ash co-doped concrete at the dosage of 255kg / Anti-abrasion ability to improve back to ordinary concrete, anti-cavitation capacity increased by 4 times. By using expansive agent in the mixed NSF agent to compensate the early shrinkage of the silica fume concrete and strengthen early wet atomization curing, the problem of early shrinkage of the silica fume concrete is solved. The successful application in the nozzle engineering proves that the NSF agent is a Promote the use of new materials.