已报道的纳米晶软磁合金Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9和Fe_(73.1)Cu_(1.2)Nb_(12.5)Si_(12.5)B_(10)显示出优良的综合软磁性能,特别是在宽频率范围内良好的磁导率频散特性
【机 构】
：
上海钢铁研究所 上海 200940
论文部分内容阅读
已报道的纳米晶软磁合金Fe_(73.5)Cu_1Nb_3Si_(13.5)B_9和Fe_(73.1)Cu_(1.2)Nb_(12.5)Si_(12.5)B_(10)显示出优良的综合软磁性能,特别是在宽频率范围内良好的磁导率频散特性和低的高频铁损可与钴基非晶合金相比,但明显优于高镍超坡莫合金和功率Mn-Zn铁氧体。但是,这两种典型的Fe-Cu-Nb-Si-B合金都含有较昂贵的铌,而且制带较困难。所以,用比铌便宜得多的元素代替铌制成
It has been reported that the Fe_ (73.5) Cu_1Nb_3Si_ (13.5) B_9 and Fe_ (73.1) Cu_ (1.2) Nb_ (12.5) Si_ (12.5) B_ (10) nanocrystalline soft magnetic alloys exhibit excellent overall soft magnetic properties, Good permeability dispersion characteristics over wide frequency range and low HF iron loss are comparable to those of cobalt-based amorphous alloys, but are significantly better than those of high-nickel super-permalloy and power Mn-Zn ferrites. However, both of these typical Fe-Cu-Nb-Si-B alloys contain more expensive niobium and the banding is more difficult. Therefore, niobium is made of a much cheaper element than niobium
其他文献
适用于磁性屏蔽的一种粉末包合有平均厚度约0.01～1μm和纵横比约1～1000的磁塑性非晶合金片,这种粉末薄片最好是大轴/小轴>1.2的扁平体。 合金组成可用分子式Fe_u M_v(Si,B)_w
日本住友电气工业公司制成目前世界上最高临界电流密度的铋系超导线。其临界电流密度值在液氮温度77.3K(-195.7℃)下达10600A/cm~2。而此前由日立制作所与日立电线公司共同
烧蚀材料能在十分苛刻的条件下承受数千摄氏度的高温,原因在于它能通过“烧蚀”发挥极其惊人的吸热、散热和隔热作用。通常每公斤烧蚀材料便可带走几千万焦尔的热量。 “烧
本文对一次烧成工艺和二次烧成法制成的n-型SrTiO_3半导瓷的非线性V-Ⅰ关系作了定性描述。着重讨论了V-Ⅰ特性曲线3个区的导电机理。根据烧成工艺,建立了改进的双层晶界势垒
(英国利物浦大学,1990年3月27、29日)复合材料性能与设计、1.酚醛GRP的固有性质K .L.Forsdyke(BP化工公司,英国)2.高模量纤维和复合材料变形的微观力学R.J.DaJ等(曼彻斯特材
永磁体R_x(Fe_(1-z)Coz)_(100-x-y-w)B_yM_w(R为钇或稀土,x=5～20,y=4～15,z=0～0.7,w=4～10,M是从Zr、Nb、Mo、Hf、Ta、W、TiCr和V中选择的一种元素)的生产方法包括:向一旋转的冷态
本文研究了Ni-14.5Cr-1.5Si(wt%)合金淬火后时效发生的无序向有序转变对合金电阻率、对铂热电势、比热的影响。结果表明:电阻率显著增加,热电势、比热增加很小。X射线衍射分
班里45人,两人一同桌。新学期一排座位,我便是多出来的那-个,没有同桌。t扭过头,每每空荡荡,直直地看到过道那边,我不由地,觉得少了些什么。上课时,同桌讨论,看着大家交换着
以固体光声效应的RG理论为依据,用光声法测量了压电陶瓷材料PZT的热参量。实验结果表明:用此方法只需要测出一个量就能同时确定PZT的α、k和C的值,并且实验设备简单,速度快,
RE-Fe-x(x=Ti, Mo, V, Zr)的机械合金化是在球磨机中于氩气内完成的,其中Fe和x的原料粒度为5～40μm, RE的粒度小于0.5 mm。研磨60 h,粉粒温度达到300～400℃,从而形成硬磁性的