一、原料与配比环氧树指1、304(防老化剂)0.3、速凝粉1~1.5(自制)碳苯胺0.15(自配)丙酮、清洗荆(用于清洗凿口)、易燃溶液剂0.25。以上均系体积比。二、配制方法(1)慢凝法将数种药物按比例分先后混合拌匀后温度调升到35℃左右,将合成药液填入裂缝凿槽内插紧压平,并用药物在表面进行保护处理。(2)速凝法按慢凝法拌匀药液后再加入易燃溶液剂快速拌匀、再填入裂缝凿槽内插紧压平,并用药物在表面进行保护处理.从加入易燃溶液药开始到用完时间不得超过15分钟。故动作要快,每次拌量宜少.三、主要优点(1)凝固时间可选择因地因工程而宜,可选择不
First, raw materials and ratio epoxy resin finger 1,304 (anti-aging agent) 0.3, quick-setting powder 1 to 1.5 (homemade) carbon aniline 0.15 (self-allocated) acetone, cleaning Jing (for cleaning chisel), flammable Solution 0.25. Above are all volume ratios. Second, the preparation method (1) slow coagulation method Several kinds of drugs were mixed in proportions and mix well and the temperature was adjusted to about 35°C. The synthetic liquid was filled into the crack chisel, and the drug was applied on the surface. Protection process. (2) Quick coagulation method Mix the liquid slowly by the slow coagulation method and then add the flammable solution quickly and mix well, then fill in the crack chisel to insert tightly and flatten, and use the drug to protect the surface. From the addition of flammable solution The time from when the medicine starts to run out must not exceed 15 minutes. Therefore, the action should be fast, and the amount of time should be less each time. Third, the main advantages (1) solidification time can be selected due to the ground due to the project and may choose not to