Preparation and Properties of PMMA Modified Silica Aerogels from Diatomite
【机 构】
:
School of Civil Engineering, Dalian University of Technology, Dalian 116024, China;School of Civil E
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2014年5期
其他文献
Tensile Strength and Oxide Analysis of Carbon Steel in Concrete Exposed in Atmospheric Environment f
The tensile strength of a corroded rebar in a 53-year-old concrete structure was studied. The microstructure of the metallic substrate, the fracture surface, and the corrosion product layers were investigated. Metallographic observation results showed tha
Structural, Optical and Electrical Properties of Li-doped ZnO Thin Films Influenced by Annealing Tem
The physical properties, the pre-reacting performance and melting properties of the loose glass batch and the granulated glass batch were investigated, respectively. The experimental results showed that compacted glass batch could reduce dust, use ultra-f
Preparation of Metakaolin Based Geopolymer and Its Three- dimensional Pore Structural Characterizati
Three types of pure geopolymer pastes (poly-sialate PS, poly- sialate-siloxo PSS, and poly-sialate-siloxo PSDS) werefi rst prepared by alkali (NaOH and KOH) activated metakaolin. Then a void space network was employed to simulate the 3-D pore-throat distr
Facile Hydrothermal Synthesis of Plasmonic Photocatalyst Ag@AgCl and Degradative Photocatalysis unde
The Oxidation State of Sulfur Detected in Na2O-CaO-SiO2 Float Glass by X-ray Absorption Near Edge St
Effect of Aggregate Gradation with Fuller Distribution on Properties of Sulphoaluminate Cement Concr
Experimental investigations on mechanical property and durability of sulphoaluminate cement concrete with aggregate gradations according to Fuller distribution are presented in this paper. Compressive strength, water impermeability and resistance capabili
In-service structural health monitoring (SHM) technologies are critical for the utilization of composite aircraft structures. We developed a Lamb wave-based in-service SHM technology using built-in piezoelectric actuator/sensor networks to monitor delamin
The aim of the present study was to investigate the influence of heavy metals on the polymorph transformation of tricalcium silicate. Heavy metal (0.1wt% to 3.0wt%) of Cr, Zn, Cu, Ni and Pb (in oxides form) was added into the raw mixtures and then sintere
Combined with DTG analysis, X-Ray diffraction analysis (XRD) andfi eld emission scanning electron microscopy analysis (FSEM) affi liated with energy dispersive spectrometer analysis (EDS), the early hydration and carbonation behavior of cement paste compa