【摘 要】
：
The annealed microstructures of the rolled AZ31 alloy sheets were examined by using light optical microscopy. The mechanical properties were measured by tensile
【机 构】
：
Key Laboratory for Advanced Manufacturing by Materials Processing Technology
论文部分内容阅读
The annealed microstructures of the rolled AZ31 alloy sheets were examined by using light optical microscopy. The mechanical properties were measured by tensile testing, with their crystal orientations analyzed by X-ray diffraction (XRD). After the annealing treatment, the elongated grains were transformed to equiaxed grains with uniform and homogeneous structures. The changes of microstructure decreased the yield strength and enhanced the elongation. The analysis of XRD shows that the AZ31 alloy sheet possesses intense basal-texture, which is weakened during the recrystallization while reinforced during the grain growth. The intense basal-texture induces low ductility, which hence makes the further rolling more difficult. The results indicate that the optimum annealing treatment during AZ31 alloys sheet rolling is at about 300 ℃ for 60-120 min.
其他文献
The characteristics of novel Nd-Fe(Ni, Co, Al)-B microstructure prepared by strip casting technique were studied. The novel microstructure was observed using sc
The mechanism of expansion of mortars and pastes with limestone filler due to external sulfate attack was studied.Mortars and pastes made at water to solid rati
A new no-reference blocking artifact metric for B-DCT compression video is presented in this paper. We first present a new definition of blocking artifact and a
A new all-zero block determination rule was used to reduce the complexity of the AVS-M encoder. It reuses the sum of absolute difference of 4×4 block obtained
YbAl3(BO3)4 crystal of good optical quality was grown by the flux method. The structure of YbAl3(BO3)4 crystal was determined by single-crystal X-ray diffractio
Based on analysis of three alloys with various Re contents, the effects of Re on the interfacial structure characteristic and interfacial dislocations of γ/γ
Two comparative models taking into account of momentum,energy and mass transport coupled with chemical reaction kinetics were proposed to simulate gas transport
Zinc aluminosilicnte glasses containing Li2 O, ZnO , Al2 O3 and SiO2 were prepared by conventional melting and quenching technique, and subsequently converted t
Age hardening characteristic and tensile property of Mg-3.5Dy-4.0Gd-3.1Nd-0.4Zr alloy were investigated. The alloy exhibits a considerable age hardening effect
In functionally graded materials (FGM), the problem of interface stability caused by the volume deformation is commonly regarded as the key factor for its perfo