A hybrid graphene-ZIF-8(G-ZIF-8) nanocomposite modified electrode was prepared in our work. SEM characterization shows that nanocrystals of zeolitic imidazolate frameworks(ZIF-8) were homogeneously well-intergrown on the surface of graphene and thus the graphene sheets were refrained from restacking, which implies the high accessible surface area. The BET results further testifies that G-ZIF-8composites had a larger surface area than 3D graphene. G-ZIF-8 modified electrode exhibited excellent electroanalytical performance for dopamine. The linear concentration range was from 3.0 mmol/L to1.0 mmol/L with the detection sensitivity of 0.34 m A/mmol/L and the detection limit of 1.0 mmol/L was obtained. The interference study, electrode stability and reproducibility were carried out. In addition, the prepared sensor was applied to the detection of DA in serum sample with recoveries from 96.8% to100.7%. It is believable that the structure characteristic of G-ZIF-8 nanocomposite is favorable for using MOFs to fabricate highly sensitive electrochemical sensor
A characterization of the nanocrystals of zeolitic imidazolate frameworks (ZIF-8) were homogeneously well-intergrown on the surface of graphene and thus the the The BET results further testifies that G-ZIF-8composites had a larger surface area than 3D graphene. G-ZIF-8 modified electrode exhibited excellent electroanalytical performance for dopamine. The The concentration of was from 3.0 mmol / L to 1.0 mmol / L with the detection sensitivity of 0.34 m A / mmol / L and the detection limit of 1.0 mmol / L was obtained. The interference study, electrode stability and reproducibility were carried out . In addition, the prepared sensor was applied to the detection of DA in serum sample with recoveries from 96.8% to 100.7%. It is believable that the structure characteristic of G-ZIF-8 nanocomposite is favorable for using MOFs to fabricate highly sensitive electrochemical sensor