The synthesis process for La 1- x Sr x Mn 1- y Co y O 3- δ ( x = 0.2, 0.3; y = 0.2, 0.8, designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC/TG, XRD, EPMA and particle size analysis methods. It was found that LSMCs were all of single phase and the synthesis process might be divided into three stages: the decomposition of reactants, the formation of LaMn(Co)O 3 based oxides, and the formation of LSMC solid solution. Typical average and the peak value of particle size, and the specific surface area are 14.65?μm, 16.4?μm and 1.38?m 2/mL, respectively, for mixed reactants and are 23.81?μm, 32.11?μm and 0.5?m 2/mL, respectively, for powder synthesized at 1?200?℃ for 8?h in air.
The synthesis process for La 1- x Sr x Mn 1- y Co y O 3- δ (x = 0.2, 0.3; y = 0.2, 0.8, designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC / TG, XRD, EPMA and particle size analysis methods. It was found that LSMCs were all of single of phase and the synthesis process might be divided into three stages: the decomposition of reactants, the formation of LaMn (Co) O 3 based oxides, and The formation of LSMC solid solution. Typical average and the peak value of particle size, and the specific surface area are 14.65 μm, 16.4 μm and 1.38 μm 2 / mL, respectively, for mixed reactants and are 23.81 μm, 32.11 ? μm and 0.5? m 2 / mL, respectively, for powder synthesized at 1? 200? C for 8? h in air.