The bonding of steel plate to Al 7graphite slurry was studied for the first time. The relationship model about preheat temperature of steel plate,solid fraction of Al 7graphite slurry, rolling speed and interfacial shear strength of bonding plate could be established by artificial neural networks perfectly.This model could be optimized with a genetic algorithm.The optimum bonding parameters are:516℃ for preheat temperature of steel plate,32.5% for solid fraction of Al 7graphite slurry and 12mm/s for rolling speed,and the largest interfacial shear strength of bonding plate is 70.6MPa.
The bonding of steel plate to Al 7graphite slurry was studied for the first time. The relationship model about preheat temperature of steel plate, solid fraction of Al 7graphite slurry, rolling speed and interfacial shear strength of bonding plate could be established by artificial neural networks perfectly . This model could be optimized with a genetic algorithm. The optimum bonding parameters are: 516 ° C for preheat temperature of steel plate, 32.5% for solid fraction of Al 7graphite slurry and 12 mm / s for rolling speed, and the largest interfacial shear strength of bonding plate is 70.6MPa.