【摘 要】
：
Many metal matrix self-lubricating composites possess excellent comprehensive properties of high strength and wear resistance after incorporating various lubricants that usually belong to ceramic phase.However,this improvement is always obtained at the co
【机 构】
：
Shenyang National Laboratory for Materials Science,Northeastern University,Shenyang 110819,China
论文部分内容阅读
Many metal matrix self-lubricating composites possess excellent comprehensive properties of high strength and wear resistance after incorporating various lubricants that usually belong to ceramic phase.However,this improvement is always obtained at the cost of notable decrease in toughness.In order to break through this toughness-tribological properties trade-off,self-lubricating composite alloys based on the matrix of FeNiCoCr0.5 high entropy alloy(HEA)were prepared by milling addition of element Co or Cr and then spark plasma sintering(SPS).Co or Cr is added into the base HEA with the aim of tailoring oxidation behavior,mechanical properties as well as tribological performances.As no ceramic lubricants are used,the alloy composites remain high toughness.Co or Cr element addition leads to the precipita-tion of a hard phase of σ-Cr and grain refinement,both of which contribute to the increase of mechanical strength.On sliding,oxidation of Fe and Ni is suppressed.Instead,the oxides of cobalt and chromium are formed upon the Co-and Cr-modified HEAs,respectively.These oxidation products,especially the oxides of cobalt that are easy to be sintered on sliding,are in favor of the formation of a lubricating glaze layer at 400℃on the worn surface,and thus the decrease in friction coefficient and wear rate,which are 0.33 and 4.0×10-5 mm3/(N m),respectively.
其他文献
Ca3-x(PO4)2 ∶xTb3+(0.2≤x≤0.4),Ca2.3(PO4)2∶0.35Tb3+,0.35A+(A=Li,Na,K),and Ca2.3(PO4)2∶0.35Tb3+,yLi+(0.35≤y≤0.455)phosphors were prepared by solid-state reaction.All the prepared phosphors formed a rhombohedral unit cell with the R3c space group.To improve
The irreversible motion of magnetic domain walls in ferromagnets can dissipate a large portion of the elastic energy,and the associated damping capacity is proportional to the magnetostriction constant.In contrast,here we found that the damping capacity o
Three-dimensional(3D)graphene-based aerogels have significant potential for adsorption,sensors,and thermal management applications.However,their practical applications are limited by their disorganized structure and ultra-low resilience after compression.
Temperature-responsive resistance transition behaviors of the melamine sponges wrapped with different graphene oxide derivatives(i.e.nanoribbon,wide-ribbon and sheet)were investigated.Melamine sponge composites coated by three types of GO derivatives were
Heterogeneous Pd nanocatalysts are efficient catalysts for the Heck reaction but require multi-step,sophisticated procedures and harsh reaction conditions.In this work,a green and facile strategy has been developed to decorate Pd nanoparticles on polydopa
Tilt probe penetrating friction stir welding(PFSW)was an innovative technology proposed in recent years to avoid the formation of kissing bond in the root of joint.However,with the heat input decreasing,“S”line or zigzag line was easily introduced in the
This work investigates the strain rate dependence of dynamic recrystallization behaviour of high-purity zinc in room temperature compression under strain rates of 10-4 s-1,10-2 s-1 and 0.5 s-1.Results from electron backscatter diffraction provide insight
Aging treatment of Cu-based alloys is essential to enhance their strength that is desirable for their exten-sive engineering applications in electrical industry,whereas the underlying mechanism of strengthening is essential for massive manufacturing of th
A valid strategy to tailor the properties of polylactic acid for more extensive applications was introducing filler.In this work,basalt fiber assembled with in-situ SiO2 nanoparticles on the surface was successfully prepared via hydrothermal method and it
Laser 3D printing based on melt growth has great potential in rapid preparation of Al2O3-based eutectic ceramics.In this work,large-scale Al2O3/GdAlO3/ZrO2 ternary eutectic ceramic rod with diameter of 4-5 mm and height higher than 250 mm was additively m