论文部分内容阅读
采用共沉淀法制备了铈锆材料(铈锆比为3/2).通过改进反应器装置(图1),延长了初始晶粒生长的时间,提高了铈锆材料的热稳定性.采用X射线衍射(XRD)、氮气吸脱附和透射电镜(TEM)对制备的材料进行了表征.结果表明,延长初始晶粒生长的时间可以得到较大尺寸的晶粒,这有利于提高材料的织构和结构性能,从而提高热稳定性.本研究将该材料应用于单Pd三效催化剂,表现出了优异的活性和热稳定性,具有良好的应用前景.“,”A series of ceria-zirconia mixed oxides (CZ-x;x=0, 20, 40 and 80) with Ce/Zr molar ratio of 3/2 were syn-thesized by co-precipitation method. In order to improve the thermal stability of ceria-zirconia mixed oxides, we ex-tended the time for the primary grain to grow up by a modified synthesis reactor. The resulting samples were charac-terized by X-ray diffraction (XRD), N2 adsorption-desorption, and transmission electron microscopy (TEM). The re-sults revealed that bigger grain could be obtained by extending time for the primary grain to grow up, which was pro-pitious to enhance the textural properties and structural properties of the materials. Thus, the thermal stability of the materials was improved. In this study, the materials were applied in the field of Pd-only three way catalysts (TWCs). The catalysts exhibited excellent catalytic performance and thermostability, showing better prospect in application.