Effects of Polycarboxylate-based Grinding Aid on the Performance of Grinded Cement

来源 :武汉理工大学学报(材料科学版)(英文版) | 被引量 : 0次 | 上传用户:yys68738464
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
A molecular modified PCE-type GA was self-synthesized, and the grindability concerning grinding duration and particle size distribution of ground cement was evaluated. Setting time, flowability, hydration heat, mechanical properties and microstructure of the ground cement were also investigated. The results show that: PCE-type GA is effective in cement grinding. With 0.03% PCE-type GA added into cement clinker, the Blain surface area reaches to the highest at every ten minutes, and the volume percent of cement particles with size of (0-32 μm) reaches the highest. Excessive amount of PCE-type GA seems to impair the grinding efficiency. The grinding efficiency promotes cement fineness and hence contributes to the cement hydration degree as well as improves the mechanical properties.
其他文献
The electrical conductivity of graphene/cement composite before and after carbonation was tested by a four-electrode method. The General Effective Media equation was adopted to fit the experiment results. EIS (electrochemical impedance spectroscopy) was e
A polarizing microscope, X-ray diffraction (XRD), fourier transform infrared spectrometer (FTIR), scanning electron microscope and energy dispersive spectrometer (SEM-EDS), X-ray photoelectron spectroscopy (XPS), and micro computed tomography (Micro CT) w
Nano-pellet α-Al2O3 was prepared using aluminum nitrate as precursor and urea as fuel by a fast method of solution combustion synthesis. The formation of the nano material was dependent on the molar ratio of fuel/oxidant, calcination temperature, and fore
Aluminum sol, dry gel, and film were prepared by sol-gel and a dipping-withdrawing method. The effect of polyethylene glycol (PEG) on the behavior of aluminum sol, gel, and film was investigated by DLS, rotary viscometer, XRD, IR, EPMA, and light microsco
A quantitative pH measuring method has been used to measure the pH of pure and blended cement mortars. The blended cement mortars incorporating supplementary cementitious materials (SCMs) such as fly ash (FA), ground granulated ballast furnace slag (GGBFS
With the risk of disappearing for the rock paintings considering long-term exposure in Helan Mountain, the freeze-thaw(F-T) cycling experiments were carried out with 12-hour F-T cycling (0, 10, 20, 30, and 40 F-T cycles) under five kinds of confining pres
TiSi2 reinforced boron phenolic composites (TP) and Vitreous silica fabric reinforced TiSi2/boron phenolic composites (VTP) were prepared by compression molding, and their thermal, mechanical, ablation properties were studied. TG results show that thermal
In order to facilitate self-compacting concrete to be better used in tunnel linings that can resist fires, a SiO2 aerogel-cement mortar coating was prepared. Based on the HC curve, a self compacting concrete cube specimens coated and uncoated with SiO2 ae
To reveal and utilize the interaction between Tamm plasmon polaritons (TPPs) and two-dimensional materials are promising for exploiting next-generation optoelectronic devices. Herein, the coupling mechanism between metal TPPs and monolayer WS2 along with
Hydration-heat-inhibiting materials(HIM) with polysaccharide as core material was prepared using microcapsule sustained-releasing technology, through a centrifugal spray granulation process after melting together. The preparation process parameters of HIM