【摘 要】
：
Fluorine doped diamond-like carbon (F-DLC) coatings were deposited on Ti-6Al-4V alloy using a hollow cathode plasma immersion ion implantation deposition system. The aim of this work is to investigate
【机 构】
：
College of Materials Science and Engineering, Chongqing University of Technology, Chongqing 400054,
【出 处】
：
第十一届全国表面工程大会暨第八届全国青年表面工程学术会议
论文部分内容阅读
Fluorine doped diamond-like carbon (F-DLC) coatings were deposited on Ti-6Al-4V alloy using a hollow cathode plasma immersion ion implantation deposition system. The aim of this work is to investigate the influence of F content on the surface morphology, structure, mechanical and tribological properties (under air and stroke-physiological saline solution) of the F-DLC coatings. The results reveal that the ratio of H/fE instead of H/E can be well predicting the anti-wear results when the F-DLC coatings have enough adhesion strength, where H is hardness, E is Youngs modulus and f is friction coefficient. The F-DLC coatings with high F content exhibit excellent tribological property under air. The low F content F-DLC coatings present super-low friction coefficient and wear rate in stroke-physiological saline solution. Reasons for the tribological property are proposed in combination with the films morphology and mechanical property.
其他文献
镍基合金Inconel718具有优良的高温、低温强度,广泛应用于航空、航天等高温、低温环境.某些Inconel718零部件使用过程中,容易与对磨副发生磨损,导致零部件尺寸改变,精度降低.本工作检测某磨损失效件,并依据德国DN50320磨损分类方法确定了其磨损失效机制.为提高Inconel718的抗磨损性能,延长使用寿命,本工作采用直线式高能离子注入技术对Inconel718材料进行表面改性,研究不
利用放电等离子烧结(SPS)技术制备了四种铜基粉末冶金摩擦材料(S1、S2、S3、S4),在对其进行力学性能和显微组织进行测试分析之后,在MM-1000Ⅱ摩擦磨损试验机上测试了四种材料在不同制动速度下的制动性能.结果 表明：采用镀铜石墨粉制备的S1、S2、S3三种材料致密度较高,且密度相差不大,均高于采用普通石墨粉制得的S4材料.S1、S2、S3三种材料的硬度远高于S4材料.采用表面经镀铜处理的石
采用离子束复合沉积技术在9Cr18轴承钢材料上制备Ag掺杂的WS2固体润滑膜,通过利用摩擦磨损试验仪对在真空封装袋中存放8年的WS2固体润滑膜试样进行摩擦性能考核,并通过FESEM、Pro-XPS、GIXRD、检测膜层的表面形貌、化学态及物相。结果 显示：所制备WS2-Ag复合润滑膜膜层致密,Ag纳米颗粒在膜层中弥散分布,该膜层具有优良的摩擦磨损性能,且复合膜经长期存放后膜层表层生成WO3、AgO
为研究高性能纤维材料切割过程中的摩擦学机理及割刀的磨损机制，设计了纤维切割性能试验台，对高性能纤维单丝切割断裂过程进行了试验研究，提出纤维单丝整个切割过程可以分为四个阶段，即弹性变形阶段、弹性压缩阶段、切割阶段和拉断阶段。通过实时检测切割过程中的切割阻力、加速度、纤维两端张紧力等的变化，结合三维形貌扫描仪对纤维断口形貌和割刀刃口进行微观形貌分析，应用摩擦学基本理论对切割过程的每阶段进行试验分析，推
The authors review materials characterization of damaged rails after the rail-wheel rolling contact friction, which have contributed to improved understanding of the microstructure evolution occurring
The in-situ formation of TiC/Ti composite coating was achieved by induction cladding (IC) approach. The powder mixture of 90wt% Ti and 10wt% graphite was preplaced on a Ti6Al4V substrate and irradiate
为提高飞机起落架耐磨损和耐腐蚀性能，超音速火焰喷涂WC-10Co4Cr涂层被认为是代替电镀硬铬层的最佳方案。本文采用团聚-瞬态烧结技术制备了四种不同WC粒度的WC-10Co4Cr喷涂粉末，其中两种仅含单一粒径的WC颗粒，另两种含有双峰粒径的WC颗粒，并用超音速火焰喷涂技术制备了四种涂层，研究了WC粒径对粉末和涂层的相组成及微观组织结构的影响规律，探究了其对涂层磨损行为和腐蚀现象的作用机理。结果 表
传统等离子喷涂技术是利用等离子电弧产生的高能量将喷涂材料加热到熔融或半熔融状态，并加速后以高速喷射于基材表面沉积其上形成涂层。利用喷涂材料与等离子气体之间的反应通过反应等离子喷涂(RPS)可沉积与喷涂材料不同的材料涂层。然而，由于反应时间有限通常获得反应物与原始粉末组成的复合材料涂层，而如何控制反应尽可能获得由反应物质为主的涂层一直是有待解决的问题。
3D printing of calcium phosphate (CaP) scaffolds has great promise to fabricate custom bone substitutes. The aim of this study is to explore one kind of CaP paste with tunable injectability and settin
When interacted with the aqueous environment, steel structures are usually prone to surface biofouling as the consequence of attachment and colonization of bacteria and other fouler species. Preventio