【摘 要】
：
采用M-2000型摩擦磨损试验机研究了铜合金的干摩擦磨损性能,在干摩擦条件下测量了不同成分铜合金与不锈钢组成的摩擦副的磨损量和摩擦系数,用扫描电镜观察其磨损表面,并对其
【机 构】
：
兰州理工大学甘肃省有色金属新材料省部共建国家重点实验室,
论文部分内容阅读
采用M-2000型摩擦磨损试验机研究了铜合金的干摩擦磨损性能,在干摩擦条件下测量了不同成分铜合金与不锈钢组成的摩擦副的磨损量和摩擦系数,用扫描电镜观察其磨损表面,并对其磨损机理进行了探讨分析。结果表明,铜合金的磨损机制主要以粘着磨损和磨粒磨损为主,在所研究的三种铜合金中,ZQAl9-4无锡青铜具有良好的耐磨性及干摩擦性能。
The friction and wear properties of copper alloy were investigated by M-2000 friction and wear tester. The wear and friction coefficient of copper alloy and stainless steel with different compositions were measured under dry friction conditions. The wear surface and friction coefficient of copper alloy were observed by scanning electron microscope , And analyzed its wear mechanism. The results show that the wear mechanism of copper alloy mainly consists of adhesive wear and abrasive wear. Among the three copper alloys studied, ZQAl9-4 Wuxi bronze has good wear resistance and dry friction properties.
其他文献
培养具有科研意识和创新精神的拔尖人才已成为我国高等教育的重要使命之一。以喀什大学化学专业为例,以本科生科研创新能力的提高为出发点,对课程设置、课堂教学、实践教学,
介绍3307-6259汽车轴类件的镦锻成形工艺及模具设计,其能够有效地解决大法兰台阶轴的成形困难问题,克服普通模锻成形工艺上的不足,大大降低原材料的消耗,提高产品的组织性能
对送风机叶轮开裂原因进行了分析,认为焊接工艺不当和运行振动是开裂的主要原因;提出了相应的焊补工艺,焊补效果良好,可为今后相同类型发电机组提供参考。
The causes of bl
本文先给出了全膜线接触弹流膜厚计算的统一公式 ,应用弹性流体动力润滑理论 ,探讨了凸轮油膜厚度的计算方法 ,利用MATLAB软件编制的程序可计算凸轮弹性流体润滑油膜厚度、凸
针对工程实际,采用直径为1.2mm的焊丝,进行了工艺性能和力学性能等多次试验,找出了一种适合于钢结构箱形梁的CO2气体保护双丝双弧自动、高效焊接方法。这种焊接方法提高了焊
目的探讨治疗预防接种局部反应的有效措施,减轻接种者的局部反应。方法将预防接种发生局部反应者46例,随机分为观察组和对照组,每组23例,观察组采用新鲜土豆片外敷,对照组采
利用OM、SEM和TEM等观察分析了未添加La和添加La的17wt%Cr铁素体不锈钢的组织和第二相;测定了塑性应变比、应变硬化指数和电化学再活化率;确定了热轧再结晶的工艺参数。结果
诊断病理学是研究疾病病因,发病机制,形态结构改变的一门基础与临床医学之间的桥梁学科,其首要任务是对疾病做出病理诊断。人体疾病的有效治疗首先取决于正确的诊断,对疾病特
以细晶高强IF钢为研究对象,在MMS-300热力模拟试验机上,利用双道次压缩实验,研究了细晶高强IF钢的静态软化行为。结果表明,变形温度越高,保温时间越长,静态软化率越大,且晶粒
从化学成分、热轧工艺、冷却工艺等方面对大壁厚海底管线钢X70进行了研制,并且研究了工艺制度对大壁厚海底管线用钢的组织和性能的影响。结果表明:采用轧后弛豫+控制冷却的工