Friction stir welding (FSW) is a new and promising welding processing that can produce low-cost and high-quality joints of aluminum alloys. 1 mm thick sheets of
【机 构】
：
Department of Materials Physics and Chemistry,Department of Materials Science
论文部分内容阅读
Friction stir welding (FSW) is a new and promising welding processing that can produce low-cost and high-quality joints of aluminum alloys. 1 mm thick sheets of 2024-T4 aluminum alloys which are always used as building and decorating materials were welded by FSW. The microstrueture and mechanical properties of friction stir welded 1 mm thick sheets of 2024-T4 aluminum alloy were studied. It was found that the thinner the 2024 aluminum alloy, the larger the FSW technological parameters field. The grains size of weld nugget zone (WNZ) is approximately 10 times smaller than that of the parent material, but the second phase in the material is not refined apparently in the welding. The FS welded joints have about 40% higher yield strength than the parent material,but the elongation of FS welded joints is under about 50% of the parent material. The electron backscattered diffraction (EBSD)results show that there are much more low angle boundaries (LAB) in WNZ than that in parent material, which indicates that FSW causes a number of sub-grain structures in WNZ, and this is also the reason of the increase of yield strength and Vickers hardness of the welded joint.
其他文献
As the important evaluation parameters concerning the spray qualities, the porosity and surface roughness of the coatings obtained by thermal spray forming have
This paper introduces a video application-aware cross-layer framework for joint performance-energy optimization,considering the scenario of multiple users upstr
Bismuth oxide has wide applications in superconductive material, photoelectric material, electronic ceramic, electrolyte, and catalysts. To produce ultrafine bi
Al-1.0%Si alloy rods containing unidirectional microstructures were fabricated by continuous unidirectional solidification (CUS) process. The crystal growth ori
To improve the cycle performance of spinel LiMn2O4 as the cathode material of 4 V class Li secondary batteries,LiNixMn2-xO4 (x=0～0.3) samples were prepared using
Porous silicon nitride ceramics with difference volume fractions of porosity from 34.1% to 59.2% were produced by adding different amount of the pore-forming ag
Equal-channel angular pressing(ECAP) of an enhanced solid-solution treated 2024 Al alloy was successfully performed at room temperature, with an imposed equival
A self-made directional solidification device was used to fabricate d 80 mm high purity aluminum ingots. SEM and AFM were used to detect the shape of grain boun
Thimble zirconia oxygen sensors were prepared with yttria stabilized zirconia(YSZ). The surfaces of the electrode,electrolyte and their interface were observed
Microstructure variation of spray-formed Si-30%Al alloy during densification process by hot pressing was studied. The results indicate that the microstructure o