用溶胶凝胶法制备了尖晶石型Co2MnO4超细粒子,用DTATG,XRD,TEM,FTIR等手段研究了Co2MnO4超细粒子的形成过程,进而用反应评价结合XRD,XPS,BET比表面积测试研究了Co2MnO4催化剂的比表面积和表面结构与其FT反应性能间的关系.结果表明,Co2MnO4超细粒子可以在较低温度(250~350℃)下形成,并具有粒度小,分布均匀等特点.用该法制备的超细粒子Co2MnO4,其催化活性明显优于相同组成的大颗粒催化剂.
The spinel Co2MnO4 ultrafine particles were prepared by sol-gel method. The formation process of Co2MnO4 ultrafine particles was studied by means of DTA-TG, XRD, TEM and FT-IR. Then the reaction was evaluated by XRD, XPS, BET specific surface area of the Co2MnO4 catalyst was studied the specific surface area and surface structure and its F T reaction between the relationship. The results show that Co2MnO4 ultrafine particles can be formed at lower temperature (250 ~ 350 ℃), and have the characteristics of small particle size and uniform distribution. The prepared ultrafine particles Co2MnO4, its catalytic activity was significantly better than the same composition of large particle catalyst.