The effects of Yb-doping on the critical current density(Jc) and the critical temperature(Tc) in YBa2Cu3O7-δ(YBCO) were investigated.Rietveld refinements of X-ray diffraction showed that Yb3+ ions had partly substituted Y sites in YBCO and the unit cell volume V decreased monotonically as x increasing.Although Tc almost had no change with increasing Yb-concentration,the increase of Jc occurred as a field was applied and displayed a maximum at x=0.08.We argued that the formation of nanometric inhomogeneity may lead to the enhancement of pinning force.
The effects of Yb-doping on the critical current density (Jc) and the critical temperature (Tc) in YBa2Cu3O7-δ (YBCO) were investigated. Rietveld refinements of X-ray diffraction analysis showed that Yb3 + ions had partially substituted Y sites in YBCO and the unit cell volume V decreased monotonically as x increasing. Although Tc almost had no change with increasing Yb-concentration, the increase of Jc occurred as a field was applied and displayed a maximum at x = 0.08.We argued that the formation of nanometric inhomogeneity may lead to the enhancement of pinning force.