The phase composition, magnetic properties i.e. coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67Co5Nd3Y6B19 alloy, inhomogeneous in the as-quenched state, crystallized after annealing at 948 K for 0.5 h and consisted of Nd2Fe14B-type, Fe2B and paramagnetic phases. The rapidly solidified Fe64Co5Nd6Y6B19 alloy contained the Nd2Fe14B-type and paramagnetic phases. The annealing of the bulk Fe67Co5Nd3Y6B19 alloy at 948 K for 0.5 h led to hard magnetic properties. However, the bulk Fe64Co5Nd6Y6B19 alloy exhibited good hard magnetic properties di- rectly after preparation.
The phase composition, magnetic properties ie coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67Co5Nd3Y6B19 alloy, inhomogeneous in the as-quenched state, crystallized after annealing at 948 K for 0.5 h and consisted of Nd2Fe14B-type, Fe2B and paramagnetic phases. The rapid solidified Fe64Co5Nd6Y6B19 alloy contained the Nd2Fe14B-type and paramagnetic phases. The annealing of the bulk Fe67Co5Nd3Y6B19 alloy at 948 K for 0.5 h led to hard magnetic properties. However, the bulk Fe64Co5Nd6Y6B19 alloy good hard magnetic properties di- rectly after preparation.