L·Fedrizzi等:Corrosion,46(8)672(1990) 试验用316L不锈钢是在1180℃连续烧结工业炉内,于溶解氨气氛下烧制而成的。添加合金元素铜的百分含量为2%、4%、9%。致密压力和烧结时间均为变量,以便测定其对烧结不锈钢在加Cl-和不加Cl-的硼酸盐缓冲溶液中电化学行为的影响。试验结果与在硫酸溶液中的电化学行为
L · Fedrizzi et al .: Corrosion, 46 (8) 672 (1990) Test 316L stainless steel is sintered in a continuous furnace at 1180 ° C in an atmosphere of dissolved ammonia. The percentage of copper added to the alloying elements is 2%, 4%, 9%. Densification and sintering times are variables to determine their effect on the electrochemical behavior of sintered stainless steel in borate buffer with and without Cl-. Experimental results and electrochemical behavior in sulfuric acid solution