论文部分内容阅读
摘要：输水隧洞一般采用全断面一次性浇注成型，在特殊部位采用分仓浇注成型，由于分期浇筑混凝土收缩性能不均等，形成新旧混凝土之间的约束，易造成结合部位混凝土出现裂缝，致使在测定施工缝位置在极限内水压力（约0.5MP）条件下出现渗水，经试验确定采用SK手刮聚脲对施工缝进行处理，取得了良好的效果。
关键词：分仓浇注，水压力，SK手刮聚脲
Abstract: water tunnel general use of the whole section one-time pouring shape, in special parts adopt points warehouse pouring shape, due to shrinkage of concrete construction stage performance not equal, the constraints of the old and new concrete form between, easy cause combine part cracks in concrete, which were in construction joints in position limit internal water pressure (about 0.5 MP) conditions appear ooze water, experiments confirm the scrape of polyurea hand SK construction joints for processing, obtain good effect.
Keywords: points warehouse pouring, water pressure, SK hand polyurea scraping
中图分类号：TV554文献标识码：A文章编号：
一、施工概况
输水隧洞成型内径为3.4m钢筋混凝土圆涵，厚度为0.35m，标号C30W10。采用分仓浇注的部位曲线半径为20m，无法采用台车进行全断面一次性浇注。
二衬施工缝中部采用BW-Ⅱ型30×40mm遇水膨胀止水条，施工缝进行凿毛并清洗干净, 遇水膨胀止水条与环形缝处止水紧密连接。为检查止水效果在施工缝中部埋设渗压计，在混凝土强度达到28天后，管中充水加压至0.5Mpa，观察施工缝渗水情况；测量渗压计的读数，分析施工缝止水效果。
通过压水试验在充水加压至0.3Mpa时，施工缝位置不同程度的出现渗水现象。
二、缝面处理
缝面30cm范围内涂刷SK手刮聚脲，中部铺设20cm胎基布，胎基布范围内SK手刮聚脲厚度4mm，其它范围内2mm。
1、基础面处理
混凝土缝面处理首先用角磨机对混凝土表面进行打磨，清除原水泥基涂层及表面的棱角，用高压水枪冲洗表面的灰尘、浮渣，待水分完全挥发后，对混凝土表面局部孔洞用按修补工艺用丙乳砂浆填补，修补完成后，再使用砂紙对混凝土表面进行打磨、清洗，要求混凝土表明平整、坚固、无孔洞。然后在距离施工缝150mm位置用混凝土切割机切2mm深的三角形。最后将缝面清洗干净，晾干。
2、界面剂施工
缝面处理完成后采用BE14专用潮湿面界面剂，这是一种100%固含量的环氧底漆，该底漆可在饱和水或干表面施工。缝面处理后在所切割完成的三角形之间(即施工缝部位300mm)，涂刷BE14界面剂，涂刷厚度要求薄而均匀，无漏涂现象。
3、涂刷SK手刮聚脲
(1)BE14界面剂表干后直接刮涂第一层SK手刮聚脲，在混凝土施工缝30cm范围内进行涂刷1～2遍，厚度1mm。保证SK手刮聚脲与混凝土之间的粘结强度大于2.5MPa。
(2)1小时内在施工缝部位200mm范围内铺盖胎基布。
(3)再涂刷2～3遍SK手刮聚脲，直至胎基布范围内SK手刮聚脲厚度4mm，其他范围内2mm。
(4) SK手刮聚脲每次涂层厚度要均匀，涂刷SK手刷聚脲时应在两小时内完成。
二衬混凝土施工缝处理示意图
三、压水试验
待手刮聚脲达到要求后，对施工缝再次进行压水试验。
8:00开始对注浆管压水，8:04压力表指针达到0.2Mpa，期间经过5次打压，在8:53持压基本稳定。后按每次0.1Mpa递增至0.5Mpa。在0.3Mpa时，期间进行三次打压后稳压；加压至0.4Mpa时，期间进行三次打压后趋于稳定；加压至0.5Mpa时，进行二次打压后趋于稳定，稳压后持压1天，施工缝部位未发现异常问题。在加压过程中管件连接接头及混凝土与管件连接部位均无水渗出。
四、结论
通过对施工缝处理，采用SK手刮聚脲能够满足输水隧洞的内水压力在0.5Mpa的情况下，施工缝位置的防水效果。保证了在特殊地段采用分仓浇注而产生施工缝的防水效果。
参考文献：
[1] 艾克拜尔买买提，马军. SK 手刮聚脲弹性体材料在水库放水涵洞明流段底板加固中的应用[J]. 内蒙古水利
注：文章内所有公式及图表请以PDF形式查看。
关键词：分仓浇注，水压力，SK手刮聚脲
Abstract: water tunnel general use of the whole section one-time pouring shape, in special parts adopt points warehouse pouring shape, due to shrinkage of concrete construction stage performance not equal, the constraints of the old and new concrete form between, easy cause combine part cracks in concrete, which were in construction joints in position limit internal water pressure (about 0.5 MP) conditions appear ooze water, experiments confirm the scrape of polyurea hand SK construction joints for processing, obtain good effect.
Keywords: points warehouse pouring, water pressure, SK hand polyurea scraping
中图分类号：TV554文献标识码：A文章编号：
一、施工概况
输水隧洞成型内径为3.4m钢筋混凝土圆涵，厚度为0.35m，标号C30W10。采用分仓浇注的部位曲线半径为20m，无法采用台车进行全断面一次性浇注。
二衬施工缝中部采用BW-Ⅱ型30×40mm遇水膨胀止水条，施工缝进行凿毛并清洗干净, 遇水膨胀止水条与环形缝处止水紧密连接。为检查止水效果在施工缝中部埋设渗压计，在混凝土强度达到28天后，管中充水加压至0.5Mpa，观察施工缝渗水情况；测量渗压计的读数，分析施工缝止水效果。
通过压水试验在充水加压至0.3Mpa时，施工缝位置不同程度的出现渗水现象。
二、缝面处理
缝面30cm范围内涂刷SK手刮聚脲，中部铺设20cm胎基布，胎基布范围内SK手刮聚脲厚度4mm，其它范围内2mm。
1、基础面处理
混凝土缝面处理首先用角磨机对混凝土表面进行打磨，清除原水泥基涂层及表面的棱角，用高压水枪冲洗表面的灰尘、浮渣，待水分完全挥发后，对混凝土表面局部孔洞用按修补工艺用丙乳砂浆填补，修补完成后，再使用砂紙对混凝土表面进行打磨、清洗，要求混凝土表明平整、坚固、无孔洞。然后在距离施工缝150mm位置用混凝土切割机切2mm深的三角形。最后将缝面清洗干净，晾干。
2、界面剂施工
缝面处理完成后采用BE14专用潮湿面界面剂，这是一种100%固含量的环氧底漆，该底漆可在饱和水或干表面施工。缝面处理后在所切割完成的三角形之间(即施工缝部位300mm)，涂刷BE14界面剂，涂刷厚度要求薄而均匀，无漏涂现象。
3、涂刷SK手刮聚脲
(1)BE14界面剂表干后直接刮涂第一层SK手刮聚脲，在混凝土施工缝30cm范围内进行涂刷1～2遍，厚度1mm。保证SK手刮聚脲与混凝土之间的粘结强度大于2.5MPa。
(2)1小时内在施工缝部位200mm范围内铺盖胎基布。
(3)再涂刷2～3遍SK手刮聚脲，直至胎基布范围内SK手刮聚脲厚度4mm，其他范围内2mm。
(4) SK手刮聚脲每次涂层厚度要均匀，涂刷SK手刷聚脲时应在两小时内完成。
二衬混凝土施工缝处理示意图
三、压水试验
待手刮聚脲达到要求后，对施工缝再次进行压水试验。
8:00开始对注浆管压水，8:04压力表指针达到0.2Mpa，期间经过5次打压，在8:53持压基本稳定。后按每次0.1Mpa递增至0.5Mpa。在0.3Mpa时，期间进行三次打压后稳压；加压至0.4Mpa时，期间进行三次打压后趋于稳定；加压至0.5Mpa时，进行二次打压后趋于稳定，稳压后持压1天，施工缝部位未发现异常问题。在加压过程中管件连接接头及混凝土与管件连接部位均无水渗出。
四、结论
通过对施工缝处理，采用SK手刮聚脲能够满足输水隧洞的内水压力在0.5Mpa的情况下，施工缝位置的防水效果。保证了在特殊地段采用分仓浇注而产生施工缝的防水效果。