Degradation phenomena like wear and corrosion, may have their effects accelerated as components operate at high temperature. The aim of this work is to make an indirect evaluation of the influence of high temperature exposure on wear behavior of Ni coatings. A Ni-Cr-Mo-W alloy, was deposited with Plasma Transferred Arc (PTA) process. An indirect approach based on the Ahrrenius relationship was used to evaluated long time exposures at high temperatures. To simulate longer exposures at lower temperatures, coatings were exposed to higher temperatures for the same time interval. So coatings were soaked in an air furnace at 650°C, 1000°C and 1200°C. Metal/metal wear behavior was evaluated by pin-on-disc tests. Pins were removed from the coatings by eletrodischarge machining and rubbed against a VC31 quenched and tempered tool steel. Two sets of wear tests were run at 2m/s, for different loads (0.5, 1.0, 2.0 and 3.0Kg) and for different sliding distances (120, 720, 1080, 1440 and 1800m).Coatings characterization was done by scanning electronic microscopy and Vickers microhardness. Results showed as temperature is increased, coatings wear performance is altered, and this is associated with microstructural changes. The aim of this work is to make an indirect evaluation of the influence of high temperature exposure on wear behavior of Ni coatings. A Ni-Cr-Mo -W alloy, was deposited with Plasma Transferred Arc (PTA) process. An indirect approach based on the Ahrrenius relationship was used to evaluated long exposures at lower temperatures, coatings were exposed to higher temperatures for the Same time interval. So coatings were soaked in an air furnace at 650 ° C, 1000 ° C and 1200 ° C. Metal / metal wear behavior was evaluated by pin-on-disc tests. Pins were removed from the coatings by eletrodischarge machining and rubbed against a VC31 quenched and tempered tool steel. Two sets of wear tests were run at 2m / s, for different loads (0.5, 1.0, 2.0 and 3.0Kg) and for different sliding distances (120, 720, 1080, 1440 and 1800m ) .C oatings characterization was done by scanning electronic microscopy and Vickers microhardness. Results showed as temperature is increased, coatings wear performance is altered, and this is associated with microstructural changes.