【摘 要】
：
通过溶液共混法制备了聚乙烯醇/海藻酸钠/多壁碳纳米管复合膜,对其进行了透光率、力学性能和DSC表征,并研究了对Cr2O27-的吸附性能。结果表明,PVA与SA等质量混合时相容性好;M
【机 构】
：
黑龙江东方学院食品与环境工程学部,黑龙江工程学院材料与化学工程学院,
论文部分内容阅读
通过溶液共混法制备了聚乙烯醇/海藻酸钠/多壁碳纳米管复合膜,对其进行了透光率、力学性能和DSC表征,并研究了对Cr2O27-的吸附性能。结果表明,PVA与SA等质量混合时相容性好;MWNTs的添加有助于提高复合膜力学性能、热性能;在pH值为2、温度为30℃、MWNTs为80mg时,吸附6h后,复合膜对Cr2O27-的去除率达到96.84%。
Polyvinyl alcohol / sodium alginate / multi-walled carbon nanotube composite films were prepared by solution blending method, and their light transmittance, mechanical properties and DSC characterization were studied. The adsorption properties of Cr2O27- were also studied. The results showed that the compatibility of PVA with SA was good. The addition of MWNTs was helpful to improve the mechanical and thermal properties of the composite membrane. At pH 2, temperature 30 ℃ and MWNTs 80mg, The removal rate of Cr2O27- reached 96.84%.
其他文献
从细乳液聚合制备有机-无机复合纳米粒子体系的助剂、聚合方法及过程和提高无机纳米粒子包覆率的措施3个方面介绍了采用细乳液聚合法制备有机-无机复合纳米粒子的最新研究进
目的：绘制“男女声录制普通话言语测听材料”中单音节和双音节词表以及短句表的言语识别率-强度函数（Performance-intensity function，P-I）曲线，获得正常人P-I函数曲线的言语识别
（焦作 沁阳公费医疗医院，河南 沁阳，454550） 【摘要】 目的：探讨分析老年性慢性阻塞性肺气肿并发自发性气胸的临床的特点。结果：168例老年慢性阻塞性肺气肿并发自发性气胸患者有3种基础疾病：慢性支气管炎（76例），支气管哮喘（54例），肺结核（38例）；发病诱因主要为呼吸道感染（112例）；气胸分型：张力型（45例），交通型（53例），闭合型（70例）；单侧（132例），双侧（36例）；肺
强碱型阴离子交换树脂应用领域广泛,但其不耐高温的缺点限制了其应用领域的进一步扩展。综述了强碱型阴离子交换树脂最新的研究现状,重点分析了一些新的提高强碱阴离子交换树
近年来,由于细胞毒性药物、免疫抑制剂、广普抗感染药物的广泛应用,真菌感染无论是在发生频率还是在致病菌种方面都在不断增加,使医院内真菌感染的发病率呈上升趋势且随着抗
采用静电纺丝法制备MgO,SiO2,Nd2O3,MnCO3与PVA膜混合物,再通过高温固相法制备长余辉发光材料MgSiO3∶Mn2+,Nd3+,对这种红色长余辉材料的发光性能进行了研究。借助SEM对其表
将聚氯乙烯(PVC)和苯胺(An)单体置于同一体系中,在乳化剂存在的条件下,分别于不同温度下以过硫酸铵(APS)为氧化剂氧化苯胺聚合,合成了聚苯胺/聚氯乙烯(PANi/PVC)复合物,并探
以花生壳为原料,采用微波预处理协同SO4-/TiO2-Al2O3固体酸水解制备乙酰丙酸.在单因素试验基础上,以水解温度、水解时间、固体酸用量为因素,乙酰丙酸得率为响应面值,设计了三
将5,5-二甲基海因接枝到壳聚糖上,添加TiO2,用涂膜的方法制备复合膜。比较分析了不同参数条件下的氯含量高低,得出最佳工艺参数,然后按照最佳工艺参数制备复合膜,对复合膜进
目的探讨研究医疗安全管理信息在医院中应用作用。方法以医院的医疗安全隐患的实例,设置医疗安全监管系统,以全生存周期理论和IPO建模方法,研制医疗隐患处理的四个结构模型模