研究了退火处理温度对无限冷硬铸铁轧辊组织和性能的影响。研究结果表明，温度低于600℃的热处理，对冷硬铸铁的宏观组织没有明显影响，但使其宏观和微观硬度降低。
The effect of annealing temperature on microstructure and properties of infinite chilled cast iron roll was studied. The results show that the heat treatment at temperatures below 600 ° C has no significant effect on the macrostructure of chilled cast iron but decreases the macroscopic and microscopic hardness.