分别以吐温80和复合乳化剂司盘80/吐温80为乳化剂,采用反相乳液法,以大豆油为油相,氯化钙(CaCl2)为交联剂制得海藻酸钠(ALG)/壳聚糖(CS)纳米微球。采用SEM和激光粒度分析仪对纳米微球的形貌和粒径进行表征。结果表明,采用复合乳化剂司盘80/吐温80适合油包水体系,制得的ALG/CS纳米微球粒子为球形;采用复合乳化剂比采用单一乳化剂制备的纳米微球粒径分散指数小;随着司盘80∶吐温80的质量配合比不同,微球的粒径随复合乳化剂中吐温80量的增加而减少,粒径分散指数PDI值在0.1~0.2之间;当司盘80∶吐温80质量配合比为1∶1.4时,制得的纳米微球平均粒径最小为364.4nm;当司盘80∶吐温80质量配合比为1∶0.2时,制得的纳米微球平均粒径最大为1171nm。
Tween 80 and emulsifier Span 80 / Tween 80 were used as emulsifiers respectively. Alginate (ALG) was prepared by reverse phase emulsion method using soybean oil as oil phase and calcium chloride as crosslinking agent ) / Chitosan (CS) nanospheres. The morphology and particle size of nanospheres were characterized by SEM and laser particle size analyzer. The results showed that the composite emulsifier Span 80 / Tween 80 was suitable for the water-in-oil system, and the prepared ALG / CS nanoparticles were spherical. Compared with the single emulsifier, The index is small; with the Span 80: Tween 80 mass ratio of different microspheres with the size of the composite emulsifier Tween 80 decreased, the particle size distribution index PDI values between 0.1 to 0.2; When the Span 80: Tween 80 mass ratio of 1: 1.4, the average particle size of the prepared nano-microspheres is 364.4nm; when Span 80: Tween 80 mass ratio of 1: 0.2, The average diameter of nanospheres is 1171nm.