Fe-3Cr-0.5Mo-0.3C and Fe-3Cr-l.4Mn-0.5Mo-0.367C sintered alloys were plasma nitrided at different temperatures. Characterization was performed by microhardness measurement, optical microscopy, SEM and XRD. Both materials had similar nitriding case properties. 1.4% manganese did not change the as-sintered microstructure considerably. It was observed that monophase compound layer, formed with increasing temperature. Compound layer thickness increased with increasing temperature while nitriding depth increased up to a level and then decreased. Core softening was more pronounced at higher temperature owing to cementite coarsening.
Fe-3Cr-0.5Mo-0.3C and Fe-3Cr-1.4Mn-0.5Mo-0.367C sintered alloys were plasma nitrided at different temperatures. Characterization was performed by microhardness measurement, optical microscopy, SEM and XRD. nitriding case properties. 1.4% manganese did not change the as-sintered microstructure impediment. It was observed that monophase compound formed with increasing temperature while nitriding depth increased up to a level and then decreased. Core softening was more pronounced at higher temperature due to cementite coarsening.