【摘 要】
：
A comprehensive experimental and numerical study of solder joints for plastic leaded chip carrier (PLCC) 84-Pin,1.27 mm pitch was carried out. The reliability o
【机 构】
：
State Key Laboratory of Advanced Welding Production Technology,Department of Material Science and En
论文部分内容阅读
A comprehensive experimental and numerical study of solder joints for plastic leaded chip carrier (PLCC) 84-Pin,1.27 mm pitch was carried out. The reliability of solder joints was assessed through accelerated thermal cycling at the temperature range of -55℃～125℃. The samples were taken out to observe the evolution in microstructure, such as grain coarsening, initiation and propagation of cracks. It was found that the Pb-rich phases segregated gradually and formed a continuous layer adjacent to the intermetallic compound (IMC) layer with increasing the number of thermal cycles, resulting in cracks near the solder/lead interface. The response of stress and strain was studied using nonlinear finite element method (FEM), and the results agreed well with the experimental data.
其他文献
The wettability in Ni / Ti ( C, N) systems with various carbides additions was investigated by the sessile drop technique. The substrates prepared by HP at 2073
It has been reported that application of pulsed biases in arc ion plating could effectively eliminate droplet particles.The present paper aims at experimental v
Antimony-doped tin oxide(ATO) nanoparticles were prepared by the mild hydrothermal method at 200 ℃ using sodium stannate, antimony oxide, sodium hydroxide and
The study on arsenopyrite and realgar of bacterial oxidation shows that the chemical behaviors of different arsenic-bearing sulphides oxidated by thermophilic b
The solidified microstructure of immiscible alloys strongly depends on the nucleation, diffusional growth, especially the coalescence of the second phase drople
Copper single crystal specimens with the longitudinal axis parallel to the [013] double-slip-orientation were grown through Bridgman technique. The fatigue test
A nickekdiimine catalyst [N, N-bis(2,6-diisopropylphenyl)-1,4-diaza-2,3-dimethyl-1, 3-butadiene nickel dibromide, DMN] was supported on palygorskite clay for et
Poly (phthalazinone ether sulfone) (PPES) with 1:1 and 1:3 ratios of bisphenol A (BPA) unit to phthalazinone unit were selected as samples. Polymer precipitatio
The density of molten Ni-W alloys was measured with a modified pycnometric method. It is found that the density of the molten Ni- W alloys decreases with temper
Continuous SiC(OAl) fibers, named KD-A fibers, were prepared by the melt-spinning of ceramic precursor polyaluminocarbosilane, air-curing, and pyrolizing at 1 3