A modified co-precipitation method for the production of Cu/ZnO/Al2O3 complex was studied. The modification was that part of Al was introduced by adding Al3+ into Cu2+/Zn2+ solution, and the rest of Al was added after co-precipitation step in the form of
【机 构】
：
Tianhua Chemical Branch, Xi’an Sunward Aeromat Co. Ltd., Xi’an 710065, China;Sanjiang Chemical Facto
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
A modified co-precipitation method for the production of Cu/ZnO/Al2O3 complex was studied. The modification was that part of Al was introduced by adding Al3+ into Cu2+/Zn2+ solution, and the rest of Al was added after co-precipitation step in the form of pseudo-boehmite. The prepared samples were characterized by different techniques such as X-ray diffraction, N2 adsorption, H2-N2O titration, temperature programmed reduction and scanning electron microscopy. X-ray diffraction characterizations revealed that Al3+ can be doped in aurichalcite lattice, and the maximum doping amount of Al3+ was 5.0％ of total Cu and Zn atoms. The Cu/ZnO/Al2O3 sample produced by the modified method, in which co-precipitated Al3+ was 2.5％ of total Cu and Zn atoms showed much better activity and stability in water-gas shift reaction than commercial sample. The high Cu surface area (26.1 m2/g) obtained by decompositon of doped aurichalcite is believed to be responsible for the activity enhancement. The stability was enhanced mainly because of the support effect of γ-Al2O3, which was decomposed from pseudo-boehmite in the calcination step.
其他文献
The crystal structure, band structure, density of states, Mulliken charge, bond population and optical properties for LiBi1-xMxO3 (M=V, Nb, and Ta) were investigated using hybrid density functional theory. It was found that LiBiO3 doped with V, Nb, and Ta
A diamond-like carbon (DLC) film was deposited on YT14 substrate using magnetron sputtering (MS). The surface morphologies, roughness and bonding spectra of obtained film were characterized using scanning electron microscopy (SEM), atomic force microscopy
The effects of circulating fluid bed (CFB) ash on the adsorption performance of polycarboxylate superplas-ticiser and the mechanism of this influence on the dispersive property of the polycarboxylate superplasticiser were investigated by determing the cem
The semisolid A356 alloy strip was prepared by a novel continuous micro fused-casting process. The microstructure evolution and mechanical property of A356 aluminum alloy strip with different nozzle temperatures were investigated. The nozzle temperature h
The water absorption and desorption processes of different types of lightweight aggregates were studied. Subsequently, the influences of pre-wetting lightweight aggregates on compressive strength, microhardness, phase composition, hydration parameters and
The effects of Cr3+,Cu2+,and Pb2+ on compressive strength,reaction products,and pore structures of fly ash based geopolymer were studied.In addition,the immobilization and bonding interaction between heavy metal and fly ash based geopolymers were investig
Plasma-enhanced CVD (PECVD) epitaxy at 200 oC was used to deposit heavy doped n-type silicon films. Post-annealing by rapid thermal processing was applied to improve the properties of the epitaxial layer. By analyzing the Raman spectra and the imaginary p
In order to investigate how to enhance the teeth fracture resistance after the post and core treatment, an in vitro study was conducted to measure the fracture resistance of endodontically treated teeth restored with cast post and core with two kinds of s
The effect of spherical particle size on the surface morphology, electrochemical property and processability of lithium iron phosphate was systematically studied. Spherical lithium iron phosphate with different particle size distributions controlled with