The effect of acicular ferrite(AF) on banded structures in low-carbon microalloyed steel with Mn segregation during both isothermal transformation and continuous cooling processes was studied by dilatometry and microscopic observation. With respect to the isothermal transformation process, the specimen isothermed at 550°C consisted of AF in Mn-poor bands and martensite in Mn-rich bands, whereas the specimen isothermed at 450°C exhibited two different morphologies of AF that appeared as bands. At a continuous cooling rate in the range of 4 to 50°C/s, a mixture of AF and martensite formed in both segregated bands, and the volume fraction of martensite in Mn-rich bands was always higher than that in Mn-poor bands. An increased cooling rate resulted in a decrease in the difference of martensite volume fraction between Mn-rich and Mn-poor bands and thereby leaded to less distinct microstructural banding. The results show that Mn segregation and cooling rate strongly affect the formation of AF-containing banded structures. The formation mechanism of microstructural banding was also discussed.
The effect of acicular ferrite (AF) on banded structures in low-carbon microalloyed steel with Mn segregation during both isothermal transformation and continuous cooling processes was studied by dilatometry and microscopic observation. With respect to the isothermal transformation process, the specimen isothermed at 550 ° C consisted of AF in Mn-poor bands and martensite in Mn-rich bands, while the specimen isothermed at 450 ° C. Two different morphologies of AF that appeared as bands. At a continuous cooling rate in the range of 4 to 50 ° C / s, a mixture of AF and martensite formed in both segregated bands, and the volume fraction of martensite in Mn-rich bands was always higher than that in Mn-poor bands. An increased cooling rate resulted in a decrease in the difference of martensite volume fraction between Mn-rich and Mn-poor bands and thus leaded to less distinct microstructural banding. The results show that Mn segregation and cooling rate strongly affect the formation of AF-containing banded structures. The formation mechanism of microstructural banding was also discussed.