【摘 要】
:
This research is focused on the study of the samples,approximatively 15 × 30 mm2 sized,that were mechanically cut from two sheets (0.4 and 0.2 mm thick,respectively) of AISI 444 Type ferritic stainless steel (FSS) (DIN 1.4521,Eu designation X2CrMoTil8-2);
【机 构】
:
Laboratorio di Metallurgia e Materiali-Dipartimento di Chimica e Chimica Industriale(LMM-DCCI), Univ
论文部分内容阅读
This research is focused on the study of the samples,approximatively 15 × 30 mm2 sized,that were mechanically cut from two sheets (0.4 and 0.2 mm thick,respectively) of AISI 444 Type ferritic stainless steel (FSS) (DIN 1.4521,Eu designation X2CrMoTil8-2);this material was in the ‘as-rolled\'state.Part of these specimens were treated superficially on one side using abrasive SiC papers with different average grit sizes (i.e.,46.2,30.2,18.3 μm) and diamond suspension (up to 1 μm) in order to obtain various surface roughness.Both the ‘as-rolled\'and superficially treated samples were then aged in a muffle furnace in static air according to a thermal cycle corresponding to the curing phase of an experimental glass used as sealing in the solid oxide fuel cell stacks.After aging,the chemical compositions and morphological peculiarities of the scale formed depending on the thickness of the samples and their surface state were studied by scanning electron microscopy,energy-dispersive spectroscopy,micro-Raman spectroscopy,bright field light optical microscopy.The obtained results show that all scales formed consist of an inner Cr203 subscale and an outer (Mn,Cr)3O4 spinel layer;the relationship between FSS grain size and scale microstructural features is consistent on the samples with mirror-like surface only;the scale thicknesses on SiC grinded samples are comparable;the scales covering the ‘as-rolled\'surfaces are morphologically similar to those grown on the surfaces finished with the 30.2 and 18.3 μm SiC papers,and their thicknesses show an intermediate situation between the abraded and the mirror-like specimens.The last described characteristics depend mainly on the surface and microstructural peculiarities resulting from the rolling process.
其他文献
Young\'s modulus is a critical parameter for designing lightweight structure,but Al and its alloys only demonstrate a limited value of 70-72 GPa.The introduction of carbon nanotubes (CNTs) is an effective way to make Al and its alloys stiffer.However,li
The influence of long-term solution treatment for various intervals on the microstructure, mechanical properties, and corrosion resistance of the as-cast Mg-5Zn-1. 5Y alloy was investigated. Variation of secondary phases was studied during solution treatm
Corrosion resistance behavior of Co-containing maraging stainless steels was investigated.Neutral salt spray and polarization test showed that maraging stainless steel with high Co content showed poor corrosion behavior.Microstructure observation proved t
Pulsed external field,including electric,magnetic,ultrasonic and laser,as an instantaneous high energy input method with high efficiency and low energy consumption,have long been known to can modify the microstructure and properties of materials.This incl
The (La4MgNi17.5Mn1.5) alloys at different melt-spun speeds were prepared by using a vacuum melt-spun furnace,and the phase structure and electrochemical properties of alloys were studied.X-ray diffraction analysis results show that melt-spun La4MgNi17.5M
The Al-2.5C master alloy is prepared to investigate the effect of the Al4C3 particle size distribution on the refining efficiency of the AZ31 alloy.The results indicate that the Al4C3 particles are potent nucleation substrates for primary α-Mg grains.With
The present work focuses on the structural stability upon hydrogenation of three typical La-Mg-Ni-based alloys: La2-MgNi9, La3MgNi14 and La4MgNi19. Structural changes during gaseous and electrochemical cycles were characterized, and the influence of the s
Open-celled porous (TiB2-Al2O3)/NiAl composites were successfully fabricated by using spherical carbamide as space holders via self-propagating high-temperature synthesis (SHS).Effects of 10Al-3B2O3-3TiO2 contents (0-20 wt%) on the pore structures and the