【摘 要】
：
研究了新型的Pd -Co催化体系催化氧化羰化苯酚合成碳酸二苯酯。当n(PdCl2 )∶n[Co(Ⅱ) ]∶n(四丁基溴化铵 )∶n(苯醌 ) =1∶1∶10∶2 5 ,T =12 0℃ ,P =2 5MPa(PCO/PO2 =4∶
【机 构】
：
华中科技大学化学系!湖北武汉430074,华中科技大学化学系!湖北武汉430074
论文部分内容阅读
研究了新型的Pd -Co催化体系催化氧化羰化苯酚合成碳酸二苯酯。当n(PdCl2 )∶n[Co(Ⅱ) ]∶n(四丁基溴化铵 )∶n(苯醌 ) =1∶1∶10∶2 5 ,T =12 0℃ ,P =2 5MPa(PCO/PO2 =4∶1) ,反应时间 8h ,PdCl2 -Co(Pyca) 2 比PdCl2 -Co(OAc) 2的催化活性高。当使用PdCl2 -Co(Pyca) 2 催化剂时 ,DPC的产率为 6 0 3%。最佳的反应温度是 12 0℃。DPC的产率随着体系的总压增加而增大。当压力升至 3 5MPa时 ,DPC产率为 8 5 3%。
A new type of Pd-Co catalyst system was developed to catalyze the oxidative carbonylation of phenol to diphenyl carbonate. When n (CoCl2): n (tetrabutylammonium bromide): n (benzoquinone) = 1: 1: 10: 2 5, T = 120 ° C and P = 25 MPa PCO / PO2 = 4: 1), reaction time 8h, PdCl2-Co (Pyca) 2 has higher catalytic activity than PdCl2-Co (OAc) 2. The yield of DPC was 6 0 3% when PdCl2-Co (Pyca) 2 catalyst was used. The optimal reaction temperature is 120 ℃. The yield of DPC increases with increasing total pressure of the system. When the pressure rose to 35MPa, the yield of DPC was 85.3%.
其他文献
吐哈盆地的天然气依据成因可划分为油型气、煤型气、混源气和生物改造气４种类型。油型气主要产于托克逊凹陷及哈密凹陷，具有δ１３Ｃ３－δ１３Ｃ２值高、δ１３Ｃ２＜－２８８和演化程度较高等特征；煤型气主要富集
随着医学科学发展和医疗技术水平的不断提高,新生儿心血管方面的疾病越来越得到重视和认识。下面就我科从1995年12月～1997年新生儿心血管疾 病25例的临床特征作如下分析。1
种是万物之源,林木良种是提高造林绿化成效的关键。一般用材林良种的遗传增效要高出普种的10%～30%,而经济林树种良种的遗传增效则更多,可数倍甚至几十倍提高其产量。数十年来,
汽化器的主要机能是按要求的最合适的空燃比把汽油混合在吸进发动机的空气中,如果把现在的复杂的汽化器换成一个比例放大式射流元件,就可简化构造,降低造价。而且因为没有浮
吉尔—130汽车大修时,转向器外壳(零件号:130—3401010)由于内圆表面上产生深划伤、裂缝和局部磨损经常被视为废品而剔出。大修外壳的技术要求规定只是在浅划伤和裂缝情况下
目前国内外在对拖拉机和机具的试验研究中都广泛采用非电量电测法。这种方法可以在田问测得各另、部件上承受的载荷和应力,压力,加速度以及其它性能参数。这样就要求测试仪
凿岩机是开发矿业的重要设备,各种凿岩机气腿是凿岩机的主要附件。气腿的重要部件——外管,长期以来靠国外进口合金铝管,要用不少外汇,更令人气愤的是帝、修、反在订货时百
本文所用符号:K——悬架弹性元件的刚度M——悬挂质量T——车架相对位移X——悬架弹性元件的变形⊿H——道路的扰动冲量,以长度为
Symbol used here: K - Stiffness of Sus
0.2～600千瓦新系列直流电动机,由ASEA和T—T A/C设计和制造。中心高200mm及以下各机座号由T—T A/C负责,中心高大于200mm的所有机座号均由ASEA负责。
0.2 to 600 kilowatts
目的:观察异体胎儿骨移植治疗小儿骨缺损的临床疗效。方法:选择孕4月以上孕妇新引产的胎儿,截取胎儿的股骨、胫骨,经制备后备用。骨不连病人,去除缺损处组织及硬化骨固定后,