【摘 要】
：
探讨了制造马口铁三片罐的150吨BOF→LF→CC工艺流程钢中T[O]、[N]含量和显微夹杂形态的演变规律。结果表明:正常坯平均T[O]含量为29.8×10-4%,[N]含量18.1×10-4%。铸坯中显
【机 构】
：
华北理工大学冶金与能源学院高品质钢连铸实验室,北京科技大学冶金与生态工程学院,
论文部分内容阅读
探讨了制造马口铁三片罐的150吨BOF→LF→CC工艺流程钢中T[O]、[N]含量和显微夹杂形态的演变规律。结果表明:正常坯平均T[O]含量为29.8×10-4%,[N]含量18.1×10-4%。铸坯中显微夹杂主要为Al_2O_3-Ca O复合夹杂、Al_2O_3-Ca S复合夹杂和少量的Si O_2夹杂,正常坯显微夹杂平均含量为8.35个/mm2,非稳态铸坯显微夹杂分别为9.78个/mm2、17.81个/mm2、14.39个/mm2,铸坯显微夹杂物含量仍然偏高,其生产工艺仍须改进之处。
The evolution of T [O], [N] content and micro-inclusions morphology in 150 ton BOF → LF → CC process steel was discussed. The results showed that the average content of T [O] was 29.8 × 10-4% and the content of [N] was 18.1 × 10-4%. The microscopic inclusions in the slab are mainly composed of Al 2 O 3 -Ca O compound inclusions, Al 2 O 3 -Ca S compound inclusions and a small amount of Si O 2 inclusions. The average content of normal inclusions is 8.35 / mm 2. 9.78 / mm2, 17.81 / mm2, 14.39 / mm2. The content of microscopic inclusions in slab is still high, and its production process still needs improvement.
其他文献
原发性肝内胆管囊性肿瘤（ＰＣＴＩＨＢＤ）比较罕见可分为囊腺瘤和囊腺癌。它们分泌大量的粘液形成单房和多房性囊肿，囊内壁发出乳头状赘生物突入囊腔，囊腺癌通常被认为由囊腺瘤恶变而来。文章报
对西昌钢钒2号高炉全捣固焦快速开炉实践进行了总结。与顶装焦相比,捣固焦显气孔率低约7%,堆比重增大约8%,燃烧失重率低约3%~5%,为此,全捣固焦开炉装料参数在顶装焦开炉装料
我们通过免疫组织化学方法对5例正常肾组织和45例肾癌组织中P53和c－myc蛋白的表达水平进行检测。结果发现：5例正常肾组织中未见这两种蛋白表达。45例肾癌中P53和C－myc阳性表达率
本文报告了２８例尘肺伴发肺癌的病理组织学及超微结构改变，一般特点是：发病年龄偏早（６４％在４１～４９岁确诊为肺癌），有中度以上吸烟史，预后差。病理特点是全部病例除尘性病变外均有支气管树上皮的慢
通过原位观察的方法,研究了H2气氛、不同温度下高磷矿还原过程的矿相结构演变规律和温度对金属铁析出形态的影响.高磷矿的鲕状结构在还原过程中未被破坏掉;随着温度的提高,矿
俗语说:外行看热闹,内行看门道。有时也未必,外行一样看得出门道来,比为讲到饮食,谢晋三大女弟子之一,著名导演鲍芝芳就有一句颇为精辟的评语——吃中有戏。这也许是一位电
自主学习以培养和发展学生的主体性为根本目的,是现代教育理念的体现,也是新课程改革的最终趋势,在教学中可通过以下途径来培养学生自主学习的能力。
The fundamental purpo
在中国正式加入世界贸易组织后的今天,居家理财也在悄然融入全球化的浪潮。随着2002年新年钟声的敲响,12个欧元国3.04亿民众,将告别他们祖祖辈辈使用的马克、法郎等货币,开
不要随便花小钱。先让我们来算一笔小帐，假如因为起床晚了，只好打出租车上班，一个月有５次的话。每次３０元钱，一个月共１５０元。也许你会认为１５０元钱不算什么，即使不花的话，也发不了财。但不要忘
钙粘蛋白Ｅ（Ｅ－ｃａｄ）是分子量为１２０ＫＤａ的细胞粘附跨膜糖蛋白，Ｅ－ｃａｄ的表达与肿瘤浸润转移呈负相关。本文概述Ｅ－ｃａｄ的生物学特性、功能调控、检测及与泌尿系肿瘤生物学行为的关系。
Cadherin E (E-cad) is