In-situ (TiCxNy-TiB2)/Ni cermets with 70 wt％ TiCxNy-TiB2 were successfully fabricated by combustion synthesis and hot pressing sintering in Ni-Ti-B4C-BN powder systems.The microstructures,density,compressive properties,and hardness of the TiCxNy-TiB2/Ni cermets with the addition of 0-8 wt％ Cr/Mo to the Ni-Ti-B4C-BN powder systems were compared and analysed.The results showed that the ceramic particles distributed uniformly in the cermets,and the size of the ceramic particles reduced with the Cr/Mo addition.Both Cr and Mo addition can improve the hardness,compressive properties,and fracture strains of the cermets.The hardness,compressive strength,and fracture strain of the (TiCxNy-TiB2)/(Ni+Cr) cermets increased from 1561HV,2.94 GPa,and 2.9％ to 1864 HV,3.65 GPa,and 3.4％,respectively when the Cr content increased to 5wt％.The hardness and compressive strength of the (TiCxNy-TiB2)/(Ni+Mo) cermets increased from 1561HV and 2.94 GPa to 1902 HV and 3.43 GPa,respectively when the Mo content increased to 8 wt％.The cermets with Cr had better compressive properties than the cermets with Mo.