A simultaneous improvement of both strength and ductility by Sn addition in as-extruded Mg-6Al-4Zn a
【作 者】
:
【出 处】
:
材料科学技术(英文版)
【发表日期】
:
0年期
其他文献
Three compositions of Ag-Cu-In-Ti system brazing alloys were designed for joining SiO2f/SiO2 ceramic composite to Nb metal.The wettability of the three alloys o
Au nanospheres modified boron-doped diamond microelectrode grown via hydrogen plasma etching solid d
Boron doped diamond (BDD) electrode is a promising electrochemical material for detecting dopamine level in the human's body.In this work,we developed a new dop
Tensile behavior of an equiaxed-grained Fe-6.5wt.%Si alloy,which was deformed into Φ6mm bar by hot rotary swaging,was investigated at various temperatures (300-
Predicting gas and shrinkage porosity in solidification microstructure:A coupled three-dimensional c
Porosity formation during solidification of aluminum-based alloys,due to hydrogen gas and alloy shrink-age,has been a major issue adversely affecting the perfor
Complex interactions within a microbial consortium can induce severe corrosion in oil pipelines.This study investigated the mechanism of microbiologically influ
Experimental investigation of a Portevin-Le Chatelier band in Ni-Co-based superalloys in relation to
The macroscopically localized deformation behaviors of Ni-Co-based superalloys with different γ'pre-cipitate content were investigated at 500 ℃ and 1 × 10-4
Microstructures of nanoporous Pd are essentially important for its physical and chemical properties.In this work,we show that the microstructures of nanoporous
Microstructure,tensile properties and mechanical anisotropy of selective laser melted 304L stainless
The microstructure and mechanical properties of 304 L stainless steel fabricated by selective laser melting are investigated in this study.With the optimized la
As concentration distribution changes have important effects on material structures and properties,con-trolling the concentration distribution is essential to a
Unveiling the underlying mechanism of forming edge cracks upon high strain-rate rolling of magnesium
In the current study,high strain-rate rolling (≥ 10 s-1) has been successfully employed to produce Mg-3Al-1Zn alloy sheets to a high reduction of 82% with a fin