【摘 要】
：
The large particle CeO2 and Y2O3 were prepared using oxalic acid as precipitator. The effects of operational parameters such as stirring velocity, precipitation
【机 构】
：
School of Materials and Metallurgy
论文部分内容阅读
The large particle CeO2 and Y2O3 were prepared using oxalic acid as precipitator. The effects of operational parameters such as stirring velocity, precipitation temperature, feeding speed, aging time, precipitation method, and calcination temperature on particle size and loose density of CeO2 were studied. Under the particular conditions, particle median size of D50≥30μm, loose density of ≥2.0 g/ml of CeO2, and particle median size of D50≥20 μm of Y2O3 were prepared. This technology had advantages of simple process, less equipment investment, ease of use, and suitability for industrialization products.
其他文献
概述了澳洲鳕鲈的生物学特性以及人工繁育研究进展情况,为今后开展澳洲鳕鲈规模化人工养殖研究提供参考。
The biological characteristics of Australian seabass perch an
Tetragonal ZrO-3 mol% YO (3Y-TZP) coated with CePOwas synthesized by a co-precipitation method and the effects of CePO content and sintering temperature on its
采用柠檬酸溶胶法合成了一系列LaMn1-xBixO3(x为0,0.1,0.2,0.3,0.4)钙钛矿型催化剂,通过X射线衍射(XRD)、比表面积测定(BET)、傅里叶红外光谱(FT-IR)、程序升温还原(H2-TPR)
扬两优6号是目前两系杂交水稻种植面积最大的组合.以两系杂交水稻扬两优6号的父母本进行机械化制种,经过几年的研究与示范,明确了机械化制种条件下,母本生长特性的变化及机械
土壤侵蚀导致水土资源及土地生产力的破坏和损失，泥沙淤积危害及其引发的一系列水环境效应已成为当前及以后一段时期内研究的热点和重点。开展流域（河流）泥沙来源研究，查明入塘、
目的以军人为被试对象自编《军人状态焦虑预测量表》(简称《量表》),用以评估不同应激条件下军人状态焦虑程度,从而为有针对性地干预奠定基础。方法选取陆军某部队的3340名军
A 40-60 t/h modularized dry coal beneficiation process with a novel method to control the bed was designed around a gas-solid fluidized bed separator. Furthermo
A series of researches were carried out for the soil samples in the Pearl River Delta under the action of consolidation loads, such as the quantitative analyses
As a part of the green process for manufacturing chromium compounds, two steps are involved in the synthesis of ultra-fine Cr2O3 powders: the first is the hydro
The characteristics of hot deformation of an α+β titanium alloy Ti-6.5Al-3.5Mo-l.5Zr-0.3Si with acicular microstructure were studied using isothermal hot comp