【摘 要】
：
Poly(4-vinylpyridine)(P4-VP) nanofiber and fluoresent poly(4-vinylpyridine)/porphyrin(P4-VP/TPPA) nanofiber were respectively prepared by electrospinning.The ef
【机 构】
：
College of Chemistry,School of Chernical and Material Engineering
论文部分内容阅读
Poly(4-vinylpyridine)(P4-VP) nanofiber and fluoresent poly(4-vinylpyridine)/porphyrin(P4-VP/TPPA) nanofiber were respectively prepared by electrospinning.The effect of the concentration of P4-VP/dimethylformamide (DMF) electrospinning solutions on the morphology of P4-VP nanofiber was investigated and it was found that the average diameter of the nanofiber of P4-VP/DMF increased with the increase of the concentration of the spinning solution.After the addition of TPPA to the P4-VP/DMF spinning solution,the diameter of P4-VP/TPPA nanofiber became even due to the increase of the conductivity of the P4-VP/DMF-TPPA solution.The photoluminescent(PL) spectral analysis indicates that the emission peak position of P4-VP/TPPA nanofiber is almost the same as that of pure TPPA at about 650 nm without peak shift,and when it was stored for 20 days,the emission peak of P4-VP/TPPA nanofiber is also at 650 rim,indicating that the fuorescent property of P4-VP/TPPA nanofiber is stable.Fourier-transform infrared(FTIR) spectrum confirms the chemical composition of the resulting P4-VP/TPPA composite nanoflber.
其他文献
The thermal decomposition of ammonium 3-nitro-1,2,4-triazol-5-onate monohydrate[NH4(NTO).H2O] wasstudied by means of thermal analysis-MS coupling and the combin
Three fluorescent indocyanines containing p-carboxybenzyl groups on N atoms in the heterocyclic rings were synthesized under supersonic. The maxima wavelength o
Precursor decomposition was used for the preparation of VTeO/SBA-15 catalyst for the selective oxidation of propane to acrolein.The catalyst shows a better perf
Two master-batches,polyamide 66 (PA66)/organo-montmorillonite (OMMT) and polyamide 6 (PA6)/OMMT,prepared by melt compounding with methyl methacrylate (MMA) as c
The typical immiscible PP/PS blend based clay nanocomposites were prepared via melt blending.The dispersion of clay was determined by X-ray diffraction (XRD) an
Coupled extensional and flexural cylindrical vibrations of a corrugated cylindrical piezoelectric shell consisting of multiple pieces of circular cylindrical su
The spherlitic structure and morphology development of poly(ethylene succinate)/poly(ethylene oxide) (PES/PEO) blends with one-step crystallization behavior wer
2,5-Di-substituted 1,3,4-oxadiazoles 3a-n have been synthesized as a one pot procedure from the reaction of acid hydrazide 1, acyl halides 2 and phosphorus pent
A new synthesized benzene nitrogen mustard was converted into glycosyl donor-trichloroacetimidate that was glycosylated with p-nitrophenol(glycosyl donors) to f