在1600℃、常压Ar气氛下,向钢液中分别加入NH4及(NH4)2C2O4,将400g钢水含铜量从0.5%分别降至0.31%及0.38%仅用脱铜剂07~0.8g.然而,如果不降低体系的压力,在相同条件下用铵盐脱铜很难将钢含量降至0.30%以下.
In 1600 ℃, atmospheric pressure Ar atmosphere, respectively, to the molten steel were added NH4 and (NH4) 2C2O4, 400g of molten steel from 0.5% copper content decreased to 0.31% and 0.38% only copper removal agent 07 ~ 0.8g. However, it is difficult to reduce the steel content to less than 0.30% by copper removal with ammonium salt under the same conditions without reducing the system pressure.