【摘 要】
：
The high calcium type stone coal from Hubei province was leached by water and dilute acid separately after being roasted with different dosage of NaCl. The water leaching rate of vanadium (WLRV) was low and only 26.8%of vanadium can be leached by water wh
【机 构】
：
College of Resources and Environmental Engineering, Wuhan University of Technology, Wuhan 430070, Ch
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The high calcium type stone coal from Hubei province was leached by water and dilute acid separately after being roasted with different dosage of NaCl. The water leaching rate of vanadium (WLRV) was low and only 26.8%of vanadium can be leached by water when 4%NaCl was added, but the acid leaching rate of vanadium (ALRV) was relatively high. Calcium in the high calcium type stone coal is greatly superfluous relative to vanadium, hence, the calcium reacts with vanadium to form Ca(VO3)2, Ca2V2O7 and Ca3(VO4)2 orderly during the stone coal roasting process and high temperature is beneficial to the reactions between calcium and vanadium, which was validated by simulated reactions between pure calcium carbonate and vanadium pentoxide. These calcium vanadates are all water insoluble but acid soluble and this causes the low WLRV and relatively high ALRV. After calcium removal by HCl, the WLRV is highly enhanced and reaches about 50%when only 2%NaCl was added. If the HCl content is too high, the stone coal is easily sintered and the formed glass structure can enwrap vanadium, which leads the WLRV to decline. Single water leaching process is not appropriate to extract vanadium from high calcium type stone coal.
其他文献
C/C composites are the emerging materials of choice for aero-engine hot-end components that will bear impact loading in thermal-oxidizing environments. For the components run for extended periods, the safe operation of components depends on how to evaluat
Cu-Ni core-shell nanowires, with an inner Cu core diameter of about 60 nm and varying Ni shell thicknesses (10, 30, 50, 60, and 80 nm), were successfully fabricated in porous polycarbonate (PC) ion-track templates by a two-step etching and electrodepositi
A new low-cost corrosion-resistant rebar (HRB400R) was designed and fabricated by chromium micro-alloying. The effects of Cr on the passivation and corrosion behavior of this rebar in the simulated concrete pore solutions were studied systematically, and
During quenching, the residual stresses are affected by the crystallographic orientation of martensite, because the nonuniform thermal stresses affect the crystallographic orientation of the lath-shaped martensite and induce the anisotropic expansion. To
The maximum principal stress, von Mises equivalent stress, equivalent creep strain, stress triaxiality in dissimilar metal welded joints between austenitic (HR3C) and martensitic heat-resistant steel (T91) are simulated by FEM at 873 K and under inner pre
The preforms with high SiC volume fraction (>50%) were successfully fabricated by two bonding methods. Moreover, the dimensional change, compressive strength, and microstructure of SiC preforms were investigated, and the bonding mechanism among SiC partic
The ultrasonic pulse signal resonance features in layered carbon fiber reinforced plastic (CFRP) within voids were researched.The frequency domain model of acoustic wave propagation in multilayered medium was established.Then the reflection coefficient of