To evaluate the retention properties of the novel ‘C’-shaped molar bands at a laboratory level. Resin-modiifed glass ionomer cement (RMGIC) was used as a luting agent for the novel C-shaped molar band. The mechanical properties of the band were examined a
【机 构】
:
Department of 0rthodontics, the Second Afifliated Hospital of Harbin Medical University, Harbin 1500
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
论文部分内容阅读
To evaluate the retention properties of the novel ‘C’-shaped molar bands at a laboratory level. Resin-modiifed glass ionomer cement (RMGIC) was used as a luting agent for the novel C-shaped molar band. The mechanical properties of the band were examined and the retention performance was characterized in the mesial, distal and vertical directions. A clinical trial was conducted using a spilt-mouth design on 50 patients. The novel C-shaped molar bands fit most molars without a repeated try-in process.The use of both nano-HA coating and RMGIC enhanced the tensile (8.00 ± 1.8 MPa) and shear strengths (27.17 ± 8.6 MPa) of the molar bands, leading to high retention in vertical, mesial and distal directions (p < 0.001). In clinical trials, the C-shaped molar bands had a failure rate (15%) comparable to that of traditional bands, and 93% of the failed bands demonstrated an adhesive remnant index score of 0, corroborating the observation that no luting agent residue remained on the tooth surface in most cases. The novel C-shaped molar bands appear to be a promising appliance that requires further clinical investigations, and may be used effectively in orthodontics.
其他文献
The core-shell structures of ZSM-5 coated with mesoporous silica were synthesized by means of dodecylamine (DDA) surfactant. The results show that the mesoporous silica shells are coated on ZSM-5 cores and result in the formation of hierarchical porous st
It was aim to investigate the interfacial microstructure and shear performance of Ti/Cu clad sheet produced by explosive welding and annealing. The experimental results demonstrate that the alternate distribution of interfacial collision and vortex of fly
The mechanical behavior and failure mechanism of recycled semi-lfexible pavement material were investigated by different scales method. The macroscopic mechanical behavior of samples was studied by static and dynamic splitting tensile tests on mechanics t
The corrosion of ECR glass ifber was investigated by the analysis methods of weight loss ratio under different acids and at various durations. Weight loss, leaching of cations, and surface composition of ECR glass ifber were analyzed. The corrosion mechan