Al-Cu-Mg-Ag alloys with different Yb contents were prepared by ingot metallurgy and thermomechanical treatment. The effect of Yb addition on the precipitation a
【机 构】
：
State Key Laboratory of Powder Metallurgy,Laboratory of Material Physics
论文部分内容阅读
Al-Cu-Mg-Ag alloys with different Yb contents were prepared by ingot metallurgy and thermomechanical treatment. The effect of Yb addition on the precipitation and microstructure of the alloys was investigated using mechanical properties testing,optical microscopy, differential scanning calorimetry(DSC), scanning electron microscopy(SEM) and transmission electron microscopy(TEM). The results show that adding 0.10%-0.35% Yb accelerates the aging hardening process, increases the maximum hardness and the tensile strength of the extruded alloys fiom room temperature to 300 ℃. Trace Yb element addition refines the grains of the casting alloys fiom 85 μm to 30 μm, decreases the precipitation temperature of Ω phase. Moreover, the addition of Yb into Al-Cu-Mg-Ag alloy decreases the precipitates size, and improves the density and the thermal stability of Ω phase between 200 ℃ and 300 ℃.
其他文献
Considering the characteristics of perovskite structure, a kinetic Monte Carlo(KMC) model, in which Bom-Mayer-Huggins(BMH) potential was introduced to calculate
Calcium-titanium-phosphate(CaTi4(PO4)6, CTP)/hydroxyapatite(HAp) is a kind of novel gradient composite bioceramics,which has excellent biocompatibility and bioa
Nanocrystalline nickel films of 17-40 nm grain sizes were prepared using pulsejet electrodeposition. Structure, corrosion and lattice strain were analysed by tr
A stable silicon dioxide film was coated on the surface of natural graphite anode by sol-gel method with Si(OCH2CH3)4,and effects of modification on performance
The cemented carbide material (YG10F) with different additions of TiC whisker (0%, 0.3%, 0.6%, mass fraction) was prepared by different techniques. The effect o
由于缺乏有效的实验手段， 目前的ＳＲＭ 颗粒轨道模型很不完善， 其中粒子的加入边界条件完全是建立在人为假设的基础上。针对这种情况， 发展了一种以实验为基础的确定凝相粒子加入边界
A simplified model was developed to describe the Curie temperature suppression of ferromagnetic nanoparticles. Based on a size and shape dependent model of cohe
A computational model combining large eddy simulation with quadrature moment method was employed to study nanoparticle evolution in a confined impinging jet. Th
The electrochemical corrosion behavior of the two Cu-40Ni-20Cr alloys prepared by conventional casting(CA) and mechanical alloying(MA) with the different grain
The green sheets with Ni paste as inner electrodes were sintered at 1 320 ℃ for 1 h under a N2/H2 mixing gas at an oxygen partial pressure p(O2)=10-8-10-12 MPa