La1.5Mg17Ni0.5 hydrogen storage materials were prepared by hydriding combustion synthesis (HCS) and mechanical alloying (MA) method respectively. The experimental results show that the hydrogen absorption properties of La1.5Mg17Nio.5 prepared by MA are better than that by HCS. La1.5Mg17Nio.5 prepared by MA can absorb 6.73 mass% hydrogen at 523 K within 1 min, and 4.92 mass% hydrogen at 423 K. The improvement of hydriding properties of La1.5Mg17Ni0.5alloy prepared by MA can be ascribed to the formation of nano-crystalline and defects during the mechanical alloying.