【摘 要】
：
本文研究了铝-硅共晶钎料经锶变质后钎料及钎缝组织和性能的变化,并考察了少量铜对变质钎料的影响。结果表明,经锶变质的铝-硅共晶钎料在机械性能、抗腐蚀性能和工艺性能几方
【机 构】
：
上海交通大学焊接教研室,上海交通大学焊接教研室,上海造船工艺研究所,
论文部分内容阅读
本文研究了铝-硅共晶钎料经锶变质后钎料及钎缝组织和性能的变化,并考察了少量铜对变质钎料的影响。结果表明,经锶变质的铝-硅共晶钎料在机械性能、抗腐蚀性能和工艺性能几方面均较未变质钎料有提高,在变质钎料中加入少量铜,可以进一步提高钎焊接头的抗腐蚀性。
In this paper, the microstructures and properties of brazing filler metal and brazed joints after strontium modification of aluminum-silicon eutectic brazing filler metal were investigated. The effect of a small amount of copper on the deterioration of brazing filler metal was also investigated. The results show that the strontium-modified aluminum-silicon eutectic solder has better mechanical properties, corrosion resistance and process properties than the un-degenerate solder, and the addition of a small amount of copper to the degenerate solder can further improve the braze joint Corrosion resistance.
其他文献
顶管生产已有近百年的历史,最老式的顶管机采用环式拔模,其生产过程实质上是一个拔制过程,金属和拔模间的阻力大,顶推负荷高。后来,环式拔模改为由3～4个被动轧辊组成的辊式机
碳钢及合金钢经过渗铬后,表面可获得一层结合牢固的铁、铬、碳的合金层(即复合碳化物型的渗铬层),该渗铬层不仅硬度高(HV1400～1800)、耐磨性好,而且还具有良好的抗腐蚀性能、
不锈钢在各种工业水中的均匀腐蚀速度很低(如316不锈钢在流速0.3—0.6米/秒海水中仅0.0005毫米/年),应具有较长的使用寿命。但实际上在各种工业水冷换热器操作中腐蚀破坏事
获省优秀论文:《新型立式沸腾冷却机的研制》《论矿山岩体分类》《微机在水泥配料中的应用》 (黄文熙) (张志呈)(吴坚李众立)获高教局优秀论文:《教育经济效果分析》 (韩立达
一般工厂对脱碳层的检查都采用金相法,但该法要破坏零件,且检验时间长。下面介绍在洛氏硬度计上测量脱碳层的方法,该法简单迅速、不破坏工件,各工厂均可采用。一、原理我们
本文介绍的铣叶片端面可调整液压夹具,用于加工图1所示的叶片零件的端面。其夹具结构见图2。该可调整液压夹具采用单件定位装夹,夹具具有可调整性,只要调换不同尺寸的定位板
采用金属清洗剂清洗金属表面油污,改善了清洗劳动条件,节省了大量清洗用油,经济效益显著。因此,近几年发展很快。为了使这项新技术健康发展,合理地选用金属清洗剂是关键,为
我厂生产的双水内冷汽轮发电机中,有不少机械零件是由35SiMn、40Cr2MoV和40Mn18Cr4等合金结构钢制成的,其中进出水系统的零件一般都采用1Cr13和1Cr18Ni9Ti不锈钢制成的。由
本文采用模拟实验法对在四辊万能轧机孔型中轧制H型钢的腿高增长规律和H型钢的腰部滑动规律进行了探讨,找出了影响腿高增长系数和滑动系数的主要因素,并分析了其影响的规律性
近日,中央党的群众路线教育实践活动领导小组印发《关于开展“四风”突出问题专项整治和加强制度建设的通知》,强调各地区各部门各单位要认真贯彻执行《党政机关厉行节约反对