研究了高纯度Fe-0.06%C-1.80%Mo和Fe-0.19%C-1.81%Mo合金在550~850℃恒温时的贝氏体转变。结果表明,转变是完全的。两种合金分别在600℃和585℃左右恒温时,转变中途出现暂时停滞的现象。而后恢复并加快转变。两合金等温等转(TTT)图均有一明显稳定区(称为河湾或θb ),θb温度上下铁素体形貌明显不同。在700~800℃恒温时,碳化物平行于奥氏体晶粒边界沉淀。
The bainite transformation of high purity Fe-0.06% C-1.80% Mo and Fe-0.19% C-1.81% Mo alloy at a constant temperature of 550-850 ℃ was studied. The result shows that the transition is complete. When the two alloys were heated at about 600 ℃ and 585 ℃ respectively, the phenomenon of temporary stagnation appeared in the transition. Then resume and accelerate the change. The two isothermal isotherm (TTT) maps have a clear stable region (called the river bay or θb), the ferrite morphology significantly different θb temperature. At 700 ~ 800 ℃ constant temperature, the carbide precipitates parallel to the austenite grain boundaries.