【摘 要】
：
对旋压态2000MPa级马氏体时效钢进行固溶、时效等不同制度的热处理试验,并进行了显微硬度测试和金相组织分析。结果表明:当固溶温度从700℃上升到850℃时显微硬度快速下降,随
论文部分内容阅读
对旋压态2000MPa级马氏体时效钢进行固溶、时效等不同制度的热处理试验,并进行了显微硬度测试和金相组织分析。结果表明:当固溶温度从700℃上升到850℃时显微硬度快速下降,随温度继续上升显微硬度变化不大;830℃×15min固溶后组织即完全奥氏体化,在830℃固溶条件下,随保温时间延长到90min,显微硬度维持在320～325 HV;480℃可视为峰值时效温度。
The heat treatment tests of different regimes of solution and aging of 2000MPa martensitic steel were carried out, and the microhardness test and microstructure analysis were carried out. The results show that the microhardness decreases rapidly when the solution temperature rises from 700 ℃ to 850 ℃, and the microhardness does not change much with the temperature increasing. The microstructure is completely austenitized at 830 ℃ × 15min, Under solution condition, the microhardness is maintained at 320 ~ 325 HV with the holding time extended to 90 min; 480 ℃ can be regarded as the peak aging temperature.
其他文献
目的 探讨18F-脱氧葡萄糖(FDG)PET/CT检查评估肝细胞肝癌(HCC)经导管肝动脉化疗栓塞(TACE)治疗后肿瘤活性及对转移灶的检出能力.方法 22例HCC患者TACE后进行18F-FDG PET/CT检
腹腔镜技术在普通外科中的应用给其带来了深刻的革命,自从第1例腹腔镜胆囊切除术(laparoscopic cholecystectomy, LC)开展以来,微创外科技术在外科领域中无论是广度还是深度
目的 分析锥形束CT(CBCT)在线摆位校正与离线自适应校正在减小头颈部肿瘤临床靶区(CTV)外放,从而减轻正常组织并发症中的作用.方法 16例行三维适形放疗的头颈部癌症患者入组.
目的:分析92例心房颤动(房颤)患者与C-反应蛋白(CRP)及其-717A>G多态性的关系。方法:采用免疫比浊法测定92例房颤患者(房颤组)和60例对照者(对照组)的血清CRP水平,同时应用聚
目的 探讨上皮中性粒细胞活化肽78(ENA-78)、干扰素诱导蛋白10(IP-10)和血管内皮生长因子(VEGF)的基因多态性与特发性肺纤维化(IPF)的相关性.方法 采用聚合酶链反应-限制片段
目的 比较两个前瞻性非随机对照直肠癌术后同步放化疗临床Ⅱ期研究的急性毒副反应及耐受性.方法 2005年3月至2007年11月分别进行卡培他滨术后同步放化疗(单药组,n=118)和奥沙
目的 分析一个遗传性凝血因子ⅩⅢ(FⅩⅢ)缺陷症家系中FⅩⅢ基因缺陷.方法 应用PCR结合直接测序法对先证者的FⅩⅢA链基因15个外显子及其侧翼序列进行分析,鉴别其中可能存在
背景:轻度认知功能损害代表阿尔茨海默病的极早期状态.磁共振波谱分析已经在阿尔茨海默病的早期诊断和鉴别诊断,以及监测病情进展和药物疗效中崭露头角,但应用磁共振波谱技术
本研究采用免疫组织化学方法,检测程度不同的慢性HBV感染者肝组织中白细胞介素17(IL-17)的表达情况,研究其表达与肝脏炎症坏死、纤维化和肝硬化的关系.
目的 探讨肿瘤转移抑制因子CD82与耐药相关蛋白LRP、多药耐药MDR1、拓扑异构酶Topo Ⅱα在不同组织结构类型的神经母细胞瘤(组织结构良好型,FH型;组织结构不良型,UFH型)中的