【摘 要】
：
In order to improve the healing performance and increase the service life of the polymer matrix composites, microcapsules were prepared by interfacial polymerization process with urea formaldehyde resin and epoxy resin E-51 as the wall material and core m
【机 构】
：
Pharmacy College, Guangdong Pharmaceutical University, Guangzhou 510006, China;School of Life Scienc
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
In order to improve the healing performance and increase the service life of the polymer matrix composites, microcapsules were prepared by interfacial polymerization process with urea formaldehyde resin and epoxy resin E-51 as the wall material and core material separately. The effects of core/shell mass ratio and emulsiifer on the distribution, topography and encapsulation rate of microcapsules were investigated. By optimizing the conditions, microcapsules with little particle size, well dispersion and compact surface were prepared. The distribution, topography, stability and compositions of the microcapsules were characterized using Nano-2s, optical microscope, scanning electron microscopy, thermal analysis and Fourier transform infrared spectroscopy. The osmosis performance of the microcapsules was evaluated. The experimental results showed that the ratio of core/shell materials (1:1) and 1% DBS as emulsifier were optimum preparation conditions and the encapsulation rate was 62.5%. The microcapsules can be synthesized successfully with mean diameter 548.6 nm and exhibit a good chemical stability below 225℃. The FTIR result indicated that urea-formaldehyde resin was formed and the core materials were successfully encapsulated in urea-formaldehyde shell. Osmosis performance evaluation showed that the microcapsules were well coated and slowly osmosed.
其他文献
Carbon nanoparticles (C-dots) were prepared by relfuxing the combustion soots of candles and corn stalk in nitric acid. The synthesized C-dots were characterized. The results showed a sharp increase in oxygen content and a sharp decrease in carbon content
The ultrafine crystalline CuCr50(Cr 50 wt%) alloys were fabricated by a combination of mechanical alloying and spark plasma sintering process. The effects of milling time on crystallite size and solid solubility of the CuCr50 composite powders were invest
A simple and green method was introduced to fabricate the electrochemical sensor based on the electrochemically reduced graphene oxide (ERGO) modified electrode. It was found that the ERGO modified electrode exhibited an excellent catalytic activity towar
Iridium dioxide with different morphologies (nanorod and nanogranular) is successfully prepared by a modiifed sol-gel and Adams methods. The catalytic activity of both samples for oxygen reduction reaction is investigated in an alkaline solution. The elec
TWIP steels with 70%cold-rolled reduction were heated at 500, 600, 700, 800, 900, 1000, and 1100℃. Then, the properties before and after heating were examined through tensile and hardness experiments. The microstructures were also analyzed by optical micr
The synthesis of Nd3+, Y3+:CaF2 nanopowder was conducted by azeotropic distillation method, which effectively dehydrated hydrous CaF2 and prevented forming hard agglomerates. X-ray diffraction (XRD), scanning electron microscopy (SEM), scanning calorimetr
A resistance random access memory (RRAM) with a structure of Ag/ZnMn2O4/p-Si was fabricated by magnetron sputtering method. Reliable and repeated switching of the resistance of ZnMn2O4 iflms was obtained between two well-deifned states of high and low res
The TiN, TiAlN, and TiAlSiN coatings were prepared on YT14 cutting tool surface with CAIP (cathode arc ion plating), the surface morphologies and phases were analyzed with FESEM (field emission scanning electron microscopy), and XRD (X-ray diffraction), r
A duplex treatment of plasma Zr-alloying and plasma nitriding was used to improve the tribological properties of Ti-6Al-4V. The microstructure of the Zr-N composite (alloyed) layer formed on Ti-6Al-4V and its hardness, friction and wear properties were in