【摘 要】
：
用慢应变速率法研究了国产17-4 PH 钢在80℃、3.5%NaCl 水溶液中的应力腐蚀开裂(SCC)行为,探讨了外加电位、预充氢和晶粒大小的影响。结果表明,晶粒大小对17-4 PH 钢的SCC 影
【机 构】
：
上海工业大学,上海工业大学,上海工业大学,上海汽轮机厂
论文部分内容阅读
用慢应变速率法研究了国产17-4 PH 钢在80℃、3.5%NaCl 水溶液中的应力腐蚀开裂(SCC)行为,探讨了外加电位、预充氢和晶粒大小的影响。结果表明,晶粒大小对17-4 PH 钢的SCC 影响不大;-850～-150 mV(SCE)为SCC 的不敏感电位区间,电位正于-150 mV(SCE)时,其破坏是阳极溶解所致,负于-850 m V(SCE)时为氢脆型SCC。文中讨论了应力腐蚀的两种机制。
The stress corrosion cracking (SCC) behavior of domestic 17-4 PH steel in 80% NaCl solution at 3.5% NaCl was studied by slow strain rate method. The effects of applied potential, pre-charging hydrogen and grain size were also discussed. The results show that the grain size has little effect on the SCC of 17-4 PH steel. The range of -850 ~ -150 mV (SCE) is the insensitive potential of SCC. When the potential is at -150 mV (SCE), the damage is anodic Due to dissolution of hydrogen embrittlement SCC at -850 mV (SCE). The paper discusses two mechanisms of stress corrosion.
其他文献
用“双套管法”淬火测定Cu:Cu-Al扩散偶中的相平衡,由于该法具有较快的冷却速度,保证了α/β相界面处于局部平衡.传统的淬火方法冷速通常是不够快的,不足以抑制β相的分解.较
本文用扫描电镜等方法确定了铌在高铬铸铁中存在的状态,并进一步阐明铌细化高铬铸铁的组织、提高机械性能和耐磨性的原因。
In this paper, the existence of niobium in hi
为了贯彻公开性原则,1989年初苏联出版了《苏共中央消志》刊物,主要介绍苏共中央机关的活动和党的领导成员的情况。该刊应读者的要求,在第5期发表了苏共总书记戈尔巴乔夫就他
文中分析薄板在三次压弯成“Л”字形零件时,板料弯曲变形断面中的应力、应变状态。采用演算法弄清了板料弯曲断面处中性层与其曲率半径的关系。确定了三步压弯成形的较佳工
现代金属切削方法中加工精度及光洁度最高的方法应首推研磨加工。如长度尺寸的精度水平达±0.025μm、球体圆度达0.25μm、柱体圆度达0.1μm、光洁度达(?)14。之所以达到如
本文通过对轧辊辊面上点的运动速度的分析,导出了三辊行星轧机的正常轧制条件及轧件不转条件,探讨了一种能保证轧件在变形区内不旋转的轧辊辊型的设计方法。
In this paper,
具有中国特色的社会主义建设道路,是我国实现高度文明、高度民主的社会主义强国战略目标的根本途径。邓小平同志指出:“把马克思主义的普遍真理同我国的具体实际结合起来,走
早在六十年代初,我国就在异步轧制方面做了很多试验研究和理论研究,针对我国带钢生产中存在的问题,在冷轧带钠的异步轧制研究方面连续取得了四项科研成果:极薄带材异步轧制新
热锯机锯齿齿形选择和设计是否合理,对锯切时的锯切功率、锯齿强度、锯片寿命、锯切噪声和锯切机生产率将有很大影响。本文在理论分析的基础上,说明选用鼠牙形齿形的优点,并
某电子乐器厂生产了一批质量低劣的童用电子琴,投放市场后销售情况不佳,于是厂长便亲自出马宣传、推销。买者:C音与D音怎么同样高? 厂长:这叫等音。买者:~#F音为何比G音还高