To develop high damping metal matrix composites, large grain size Barium titanate (BaTiO3) ceramic was sintered and added into Al powder to fabricate BaTiO3/Al composites through the powder metallurgy method and hot extrusion.The damping properties of BaTiO3 ceramic, Al matrix and BaTiO3/Al composites was examined by Dynamic Mechanical Analysis in the temperature range from 273K to 573K.The results show that although BaTiO3 exhibits high damping (Tanδ=0.12) below 400K, the damping capacity of 10 wt% BaTiO3/Al composites below 400K was not increased, compared to the Al matrix.On the other hand, the tensile strength of the composite was 42% increased from the Al matrix.The failure of exerting the intrinsic damping of BaTiO3 particles in the composites is attributed to the poor interface bonding between the particles and the matrix.