5. Giant magnetoimpedance in Fe73.5Cu1Nb2V1Si113.5B9nanocrystalline ribbons

Giant magnetoimpedance in Fe73.5Cu1Nb2V1Si113.5B9nanocrystalline ribbons

来源 :2014中国功能材料科技与产业高层论坛 | 被引量 : 0次 | 上传用户：qq310474070

【摘 要】

：

In the present work, the giant magnetoimpedance effect has been found in Fe73.5Cu1Nb2V1Si13.5B9 nanocrystalline ribbons.The optimum annealing temperature for obtaining largest GMI is about 550℃.

【作 者】

：

Huaigu Hu Yangming Hao Chunjing Gao Yanzhao Wu Feifei Liang 

【机 构】

：

Department of Physics, College of Sciences, Tianjin University of Science & Technology, Tianjin 3004

【出 处】

：

2014中国功能材料科技与产业高层论坛

【发表日期】

：

2014年2期

【关键词】

：

Magnetoimpedance effect permeability FeCuNbVSiB nanocrystalline 

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　In the present work, the giant magnetoimpedance effect has been found in Fe73.5Cu1Nb2V1Si13.5B9 nanocrystalline ribbons.The optimum annealing temperature for obtaining largest GMI is about 550℃.

其他文献

The Effect of Saponification Time on the Physical Properties of Mineral Oil-Based Magnetorheological

This overall objective of this work was to investigate the influence of saponification time on the physical property and microstructure of MR greases.With this aim, three mineral oil-based magnetorheo

会议

Magnetorheological GreaseSaponification TimeThermal StabilityPhysical Propert

高疏水聚氨酯泡沫的制备及吸油性能研究

本文通过纳米氧化锌(ZnO)修饰聚氨酯(PU)泡沫和硬脂酸改性ZnO,简便地制备了疏水亲油性质的PU吸油材料,并进行了接触角的表征和吸油性能测试。结果表明,实验制备的ZnO纳米粒子-PU (ZnO NPs-PU)泡沫和ZnO纳米棒-PU泡沫(ZnO NRs-PU)均表现出优良的疏水亲油性能和较强的吸油能力。

会议

纳米氧化锌聚氨酯泡沫疏水性亲油性吸油

刺激响应性静电纺丝纤维及其应用

刺激响应性电纺纤维因其优异的功能成为当前研究的热点。从物理刺激响应和化学刺激响应性能方面，结合纳米纤维的组成，结构，综述了电纺纤维的制备及性能。同时，讨论了刺激响应性电纺纤维在再生医学工程和药物植入释放方面的应用。结合多组分功能化，多刺激响应性的纳米纤维可望成为今后开发的方向。

会议

刺激响应性静电纺丝纳米纤维应用

30CrMnSiNi2A钢连续激光辐照性能变化的微观形貌结构分析

以14.5W/cm2的连续激光辐照30CrMnSiNi2A钢，通过改变激光辐照时间、辐照次数和样品所处环境，获得合金试样的温升历程.用X-射线衍射、扫描电子显微镜、能谱仪和纳米压痕等手段对样品的微观形貌和性能进行表征，发现样品断口均具有氧化膜-脆硬层-基体三层结构特点，脆硬层硬度高于基体，韧性低于基体.

会议

30CrMnSiNi2A钢连续激光辐照效应微观形貌

Ferroelectric and piezoelectric properties of Ba (Ti0.89 Sn0.11)O3thin films prepared by a sol-gel m

We designed a new sort of Pb-free ferroelectric film: Ba (Ti0.89Sn0.11) O3 (BTS) with a chemical constitution at the quasi-quadruple point where the four phases: Cubic, Tetragonal, Orthorhombic, Rhomb

会议

BTS thin filmswater dosageferroelectricitypiezoelectricity

Influence of FRP Waste on the Properties of Unsaturated Polyester Resin Based Artificial Marble

There is a lot of glass fiber reinforced plastic (FRP) waste every year.Its low utilization rate and serious secondary pollution cause many problems.In this paper, FRP waste was added to enhance unsat

会议

FRP wasteUnsaturated polyester resinArtificial marbleMechanical propertyCont

Inconel 625合金表面热扩散涂层在氯化物熔盐中腐蚀行为研究

在太阳能热发电储热系统中,氯化物混合熔盐比单熔盐有更高的转化效率,但是同样存在强腐蚀性问题。本文通过在镍基高温合金钢Inconel625表面热扩散渗铬与渗铝,然后经预氧化使合金表面形成氧化铬与氧化铝保护膜,研究其合金在900℃二元混合氯化物熔盐中的腐蚀行为,采用带有能谱的扫描电镜分析腐蚀产物与形貌,XRD分析产物组成。

会议

氯化物混合熔盐腐蚀热扩散渗涂层氧化膜

二元非离子表面活性剂体系的吡咯界面聚合研究

在二元非离子表面活性剂介入下，采用化学氧化界面聚合法，在0-5℃下制备聚吡咯膜。研究了Span80/Tween80复配体系对聚吡咯成膜的影响，并利用红外光谱测试、扫描电子显微镜测试、循环伏安和交流阻抗对聚吡咯膜的性能进行表征。

会议

界面聚合聚吡咯表面活性剂比电容阻抗

昭通无烟煤超高温制备优质碳材料研究与展望

研究了采用超高温石墨化法,无需其他任何附加工艺和添加催化剂等,一次性制备品质优良的人造石墨、类石墨增碳剂和高级还原剂等碳材料,并对碳材料进行了化学成分分析,颗粒堆积电阻率测试,XRD物相组成及石墨化程度测试,SEM微观结构形貌表征和拉曼散射晶化程度和晶体缺陷表征,同时还对超高温石墨化法进行了展望。

会议

昭通无烟煤超高温石墨化碳材料

Effects of Ni/Co Metal Binder Phase on Mechanical Properties of Ti(C,N)-based Cermets

Ti (C,N)-based cermets were prepared by pressureless sintering using micron-sized TiC and TiN powders as main starting materials and Ni and Co as metal binder.The fracture micrographs of Ti (C,N)-base

会议

Ti (CN)-based cermetsMetal binder phaseMechanical propertiesFracture microgr