【摘 要】
：
254SMO is a typical austenitic stainless steel with 6% molybdenum which gives possible poor oxidation resistance property at high temperature.It may affect the hot working of 254SMO.The high temperatu
【机 构】
：
BaoSteel Desheng Stainless Steel Ltd.,Fuzhou 350601,Fujian,China;Institute for Structural Materials,
论文部分内容阅读
254SMO is a typical austenitic stainless steel with 6% molybdenum which gives possible poor oxidation resistance property at high temperature.It may affect the hot working of 254SMO.The high temperature oxidation behavior of super-austenitic stainless steel 254SMO was investigated at 900 ~ 1 200℃,which is the temperature range of its hot working,in air by means of the method of mass gain,SEM/EDS and XRD.The results show that oxidation kinetics basically obeys parabolic law well.Oxidation mass gain is considered of different pattern at disparate scale of temperature with time.At the test temperatures,the oxidation layer is mainly composed of two different classes.One class is Fe2O3,and the other is Fe3O4,a variety elements involved in the formation of oxides.The former type is decreased as the temperature grows,and the latter class will be gradually disappeared at temperature above 1 050℃,and the worse oxidation resistance property is appeared at 1 050℃ and 1 100℃.As a result,the sensitivity to aging temperature of 254SMO is found.The oxide of Mo to volatilize,which is the main factor,causes the break of the continuity of oxides layer and increases the oxidation rate.
其他文献
Carborundum of the sample is determined by potassium fluosilicate titration.The Al2O3-SiC-C brick sample was melted with KOH and KNO3 in the nickel-rucible.Through the experiment,chose the best melt c
Generally,microstructures of coiled hot-rolled strips of micro-alloyed high-strength steel grades are quite complex and not easily quantifiable by conventional methods such as light optical microscopy
A novel stand alone bend testing device is used to determine elastic and plastic parameters of sheet metals.This method is applied where uni-axial tensile tests cannot be used to take into account the
A large scatter in impact energies was found in four Charpy V-notch impact samples taken from BC850 hot-rolled steel and tested under same conditions i.e.experiment temperature ( - 20℃ ) and impact fo
Surface peeling defect occurred in stamping process.QSTE500TM high strength hot-rolled sheet manufactured by Baosteel was applied.A layer of certain substances similar to slag is found underneath the
Determination of the threshold stress intensity for stress corrosion cracking (KIscc) of narrow areas such as weld and heat affected zone ( HAZ) of a weldment is a non-trivial task,because of requirem
Corrosion behaviour of low-alloy steel containing 1% Cr ( 1Cr) with normalized ( ferritic- pearlitic ) and quenched-and-tempered ( tempered martensitic ) microstructures was investigated in CO2 enviro
热挤压是无缝钢管的先进生产工艺，扩孔工序是挤压前准备空心钢坯的重要中间工序,而扩孔时钢坯温度对扩孔工艺有很大影响.通过计算机模拟和现场试验,研究了不同钢坯温度分布在扩孔工艺中的影响,得出的结论是钢坯温度呈径向温度线性变化,并且内表面温度低于外表面温度的温度场形态,有利于扩孔过程中的稳定性;作为影响扩孔精度的关键因素之一,钢坯的温度分布在钢坯内表面温度低于外表面温度的状态下,有利于减小扩孔余料的大小
Recent pipelines have utilized API Grade X-70 or X-80 for onshore installations and typically heavy wall API X-65 0ffshore for deep water offshore pipelines.However several new projects require capaci
The weldability of the commercial duplex stainless steel B2101,B2304,B2205 and B2507 is discussed.Suitable welding methods,filler metals,thermal cycles and proper shielding and root gases are recommen